Abstract:Polyimide-block-poly(dimethyl siloxane) copolymer was synthesized by a two-step process, initiated by coupling anhydride terminated poly(amic acid), AT-PAA with amino terminated poly(dimethyl siloxane), (NH 2 ) 2 -PDMS to form poly(amic acid)-block-poly(dimethyl siloxane). The resulting copolymer is then thermally treated to produce polyimide-block-poly(dimethyl siloxane), PI-PDMS. Because of the high glass transition temperature, Tg of polyimide, it is usually cured at a high temperature of about 300°C for over 2.5 h. Copolymerization of polyimide with polysiloxane, reduces the imidization temperature while maintaining high thermomechanical properties. A series of instruments were used to monitor the progress of copolymerization. The time-based analysis of the product of copolymerization enables the optimization of the structure and properties of the copolymers. The chemical structure and composition of the copolymer were studied by Fourier Transform Infrared Spectroscopy, (FT-IR). The incorporation of PDMS blocks into the copolymer and the degree of imidization of the polyimide block increased with increasing reaction time. The change in the viscosity of the copolymerizing solution was monitored by simple shear viscometry conducted with the Brookfield Viscometer. The reported increase in solution viscosity with increasing copolymerization time is associated with increasing molecular weight of the copolymer. The intrinsic viscosity of the copolymer solution was measured as a function of copolymerization time and it was found that the intrinsic viscosity of the copolymer solution increased with increasing reaction time. The glass transition temperature (Tg) and the thermal stability of the copolymer were determined by differential scanning calorimetry, DSC and thermogravimetric analysis, and TGA, respectively. Between 25°C and 420°C, the copolymers synthesized in this study show two glass transition temperatures due to the polyimide, PI block at around 380°C and another peak associated with PDMS plasticized polyimide at about 290–300°C. The two Tg peaks observed in the DSC thermogram are believed to be indicative of the structure of a block copolymer. TGA analysis shows that the thermoxidative stability of the copolymers increased with increasing reaction time, due to the incorporation of increased amount of PDMS unit into the copolymer. The combination of increasing molecular weight of copolymer, higher degree of imidization of polyimide blocks and enhanced thermoxidative stability may translate into improved flame retardancy of copolymers. This suggested enhancement in flame retardancy in air atmosphere, is believed to be due the incorporated PDMS blocks, which can be converted into silica, SiO2, a recognized thermally stable material.

Synthesis and thermal stability of a novel acetylene end-capped silicon-containing polyimide coupling agent with a silane pendant group

Novel Diacetylinic Aryloxysilane Polymers: A New Thermally Cross-Linkable High Temperature Polymer System

Synthesis and Characterization of a Novel Heat Resistant Epoxy Resin Based on N,N′-bis(5-hydroxy-1-naphthyl)pyromellitic Diimide

Silica/polyimide Hybrids and Their Dielectric Properties. I. Preparation with an Improved Sol–gel Process with Poly(amic Acid) As the Precursor

Ring-Opening Copolymerization of Mixed Cyclic Monomers: A Facile, Versatile and Structure-Controllable Approach to Preparing Poly(methylphenylsiloxane) with Enhanced Thermal Stability

The Effect of Silane Coupling Agent Containing Methacryloxy Group on UV-Curable Acrylate-Modified Polyurethane/SiO2 Hybrid Coatings

Phenylethynyl and Phenol End-Capping Studies of Polybiphenyloxydiphenylsilanes for Cross-Linking and Enhanced Thermal Stability

Melt fluidity and thermal property of thermosetting siloxane-containing polyimide resins and their organic/inorganic hybrid characteristics

Phenylethynyl-terminated Oligoimides Based on Bis(p-Aminophenoxy)dimethyl Silane: Effect of Siloxane Structure on Processability and Thermal Stability

Synthesis and properties of silicon-containing poly(diethynylbenzen-co-phenoxyphenoxybenzenediacetylene)s

Design of novel silicon-containing alkynyl diamines and their related thermosetting polyimide resins

Synthesis and properties of acetylene-terminated isoimide and imide oligomers exhibiting excellent solubility behaviors in low boiling point solvents

Synthesis and Characterization of Biphenyl Polyimide Containing Alkyl Sulfide Structure

Cure Kinetics and Thermal Decomposition Behavior of Novel Phenylacetylene-Capped Polyimide Resins

Synthesis of Polyimide-Siloxane Copolymers and Their Properties

Preparation, cure kinetics, and thermal properties of novel acetylene terminated silazanes

Synthesis and characterization of a carborane-containing monofunctional imide monomer as a modifier for imide oligomer

High Thermally Stable and Melt Processable Polyimide Resins Based on Phenylethynyl-Terminated Oligoimides Containing Siloxane Structure

Novel Polyimide-block-poly(dimethyl siloxane) copolymers: Effect of time on the synthesis and thermal properties

Curing kinetics and thermal properties of [2,2] paracyclophane/bisphthalonitrile-terminated imide resins

Effect of the Presence of a Silane Coupling Agent on Reaction Kinetics of Cationic Thermopolymerization of Epoxy Resin Adhesive