Corrosion and Stress Corrosion of 5000-Series Al Alloys in Marine Environments
R. B. NIEDERBERGER,J. L SIL,G. T. BEDFO,J. L BASIL,G. T. BEDFORD
DOI: https://doi.org/10.5006/0010-9312-22.3.68
1966-03-01
CORROSION
Abstract:The 5000 series nonheat-treatable aluminum magnesium alloys are recognized as superior to other high-strength aluminum alloys for marine applications. However, a potential corrosion and stress corrosion hazard exists in these alloys from inter-granular precipitation of a magnesium-aluminum compound. This paper summarizes results of several long-term investigations of the effect of material condition on relative corrosion and stress corrosion behavior of representative alloys.Studies involving sea water exposure were conducted with plain and welded samples of Alloys 5083, 5086, 5154, 5356 and 5456. Several tempers and sheet gages were included, with exposure times up to five years for stressed and seven years for unstressed samples. General corrosion damage was mild, characterized by scattered shallow pitting. No stress corrosion cracking was encountered in standard mill tempers. However, sensitization of materials by holding one week at 212 F (100 C) to simulate long-time natural aging did result in stress-corrosion cracking at the weld fusion line of welded and stressed 5456-H24 samples within one year. Unstressed, sensitized samples of the same alloy showed no more than normal scattered pitting.Studies of stress corrosion in marine atmosphere, with exposure times up to ten years, have been conducted with a series of experimental alloys. Variables included composition (4, 5, 6 and 7 percent magnesium, with and without manganese and chromium); temper (0, H12, H16, H32 and H36); and natural aging time (0, 1 and 3 years prior to exposure). Failures were confined almost entirely to the 6 and 7 percent magnesium alloys. Results indicate: (a) H12 and H32 tempers are more likely to fail than H16 and H36 tempers; (b) time-to-failure is a function of over-all aging time rather than exposure time; and (c) small amounts of manganese and chromium significantly reduce susceptibility of alloys to stress corrosion.Studies of the experimental alloys have been supplemented by tests up to five years' with Alloy 5456 in nine tempers, with and without sensitization. Failures occurred only in sensitized materials in H12, H16, H32 and H36 tempers and developed in a matter of days. No failures occurred in sensitized or unsensitized samples in O, H22, H24 or H321 tempers.Results confirm the excellent marine corrosion properties of commercial 5000-series alloys and indicate that caution in selection and use of these alloys is required in a few areas only.
materials science, multidisciplinary,metallurgy & metallurgical engineering