Microstructure and Mechanical Properties of (TiZrHf)50(NiCoCu)50 High Entropy Alloys

Chih-Hsuan Chen,Yue-Jin Chen,Jia-Jyun Shen

DOI: https://doi.org/10.1007/s12540-019-00383-3

IF: 3.451

2019-07-26

Metals and Materials International

Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">The microstructure and mechanical properties of pseudo-binary (TiZrHf)<sub class="a-plus-plus">50</sub>(NiCoCu)<sub class="a-plus-plus">50</sub> high entropy alloys (HEAs) with B2 matrix were investigated in this study. The studied HEAs includes Ti<sub class="a-plus-plus">40</sub>Zr<sub class="a-plus-plus">10</sub>Ni<sub class="a-plus-plus">40</sub>Co<sub class="a-plus-plus">5</sub>Cu<sub class="a-plus-plus">5</sub>, Ti<sub class="a-plus-plus">30</sub>Zr<sub class="a-plus-plus">20</sub>Ni<sub class="a-plus-plus">30</sub>Co<sub class="a-plus-plus">10</sub>Cu<sub class="a-plus-plus">10</sub>, Ti<sub class="a-plus-plus">25</sub>Zr<sub class="a-plus-plus">25</sub>Ni<sub class="a-plus-plus">16.67</sub>Co<sub class="a-plus-plus">16.67</sub>Cu<sub class="a-plus-plus">16.67</sub>, Ti<sub class="a-plus-plus">30</sub>Zr<sub class="a-plus-plus">10</sub>Hf<sub class="a-plus-plus">10</sub>Ni<sub class="a-plus-plus">30</sub>Co<sub class="a-plus-plus">10</sub>Cu<sub class="a-plus-plus">10</sub>, Ti<sub class="a-plus-plus">20</sub>Zr<sub class="a-plus-plus">15</sub>Hf<sub class="a-plus-plus">15</sub>Ni<sub class="a-plus-plus">20</sub>Co<sub class="a-plus-plus">15</sub>Cu<sub class="a-plus-plus">15</sub>, and Ti<sub class="a-plus-plus">16.67</sub>Zr<sub class="a-plus-plus">16.67</sub>Hf<sub class="a-plus-plus">16.67</sub>Ni<sub class="a-plus-plus">16.67</sub>Co<sub class="a-plus-plus">16.67</sub>Cu<sub class="a-plus-plus">16.67</sub>. XRD and SEM analyses revealed that all studied HEAs were a mixture of B2 and C15 intermetallic phases, instead of a single solid solution, due to their highly negative enthalpy of mixing and the relatively large difference in atomic radii. The B2 matrix was found capable of forming a solid solution of all six elements in a wide composition range. The lattice constants of B2 and C15 phases increase linearly with increasing the difference in atomic radii. Additionally, the microhardness of these HEAs increases from 409 to 595 HV with the increasing difference in atomic radii as well. Compression tests demonstrated substitution of Zr with Hf can improve the ductility. In all studied HEAs, the Ti<sub class="a-plus-plus">30</sub>Zr<sub class="a-plus-plus">10</sub>Hf<sub class="a-plus-plus">10</sub>Ni<sub class="a-plus-plus">30</sub>Co<sub class="a-plus-plus">10</sub>Cu<sub class="a-plus-plus">10</sub> HEA achieves a great balance between yield strength, ultimate compressive strength, and fracture strain of 1574 MPa, 1933 MPa, and 6.5%, respectively.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic </h3></span>

materials science, multidisciplinary,metallurgy & metallurgical engineering