Abstract:Nitrogen-alloyed austenitic stainless steel QN1803 (2.0%Ni-3.5%Ni) has been developed to replace the conventional 304 stainless steel (8%Ni). Both the microstructure and the corrosion resistance of both types of stainless steels in the annealed state have been extensively studied, whereas those in the cold strained state have not been studied sufficiently. The aforementioned stainless steels often undergo cold forming processes during industrial applications, such as straightening, leveling, and bending, etc., which may lead to the changes of microstructure and corrosion resistances as well as the performance. In this study, the tensile tests were performed with different tensile strains for both nitrogenalloyed QN1803 and the conventional 304 stainless steels. The microstructure and strengthening, as well as the toughening mechanisms were investigated using EBSD, XRD, and TEM. The corrosion resistance and its mechanism under different tensile strains were evaluated and analyzed via electrochemical workstation, acid corrosion tests, OM, and SEM. Notably, the microstructures of both QN1803 and 304 stainless steels are changed from dislocation plugging to a' martensite with the increase in tensile strain. The yield strength of QN1803 stainless steel is 26% higher, while its elongation is 6.6% lower than that of 304 stainless steels, respectively. This could be attributed to both the higher nitrogen content and the lower transition temperature of 50% martensite induced by 30% strain (M-d30) for QN1803 stainless steel as compared with that for 304 stainless steel. As a result, the volume fraction of the strain-induced martensite for QN1803 stainless steel under tensile strain is lower, leading to the lower toughening effect than that of 304 stainless steel. Interestingly, the experiments show that the tensile strain has a minor effect on the intergranular corrosion whereas noticeably negative effect on both the pitting and the sulfuric acid corrosion resistances of both stainless steels. Not surprisingly, 304 stainless steel undergoes a more remarkable decrease in both the pitting and the sulfuric acid corrosion resistances with the increase in tensile strain as compared with QN1803 stainless steel. This could be well understood since martensite could lead to the destruction or deterioration of the passive film on the stainless steel surface, producing an unstable dissolution-generation state during corrosion, thus reducing the corrosion resistance after tensile deformation. In conclusion, the yield strength is enhanced, ductility is slightly impaired, and both the pitting and the sulfuric acid corrosion resistances under tensile deformation are improved by nitrogen alloying. Based on these technical advantages, together with the nickel saving effect, QN1803 stainless steel has been applied in various industrial areas, such as building, construction, and home appliance, etc.

Significance of Partial Substitution of Carbon by Nitrogen on Strengthening and Toughening Mechanisms of High Nitrogen Fe-15Cr-1Mo-C-N Martensitic Stainless Steels

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

Simultaneously Enhancing Strength, Ductility and Corrosion Resistance of a Martensitic Stainless Steel via Substituting Carbon by Nitrogen

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Modulus Softening During the Γ→ɛ Martensitic Transformation in Fe–25Mn–6Si–5Cr–0.14N Alloys

Effect of Tensile Deformation on Microstructure and Corrosion Resistance of High Nitrogen Austenitic Stainless Steels

Microstructure evolution and mechanical properties of martensitic stainless bearing steels with different carbon nitrogen ratios

Effect of Nitrogen on Precipitate Characteristics and Pitting Resistance of Martensitic Stainless Steel

Influence of Grain Boundary Carbides on Mechanical Properties of High Nitrogen Austenitic Stainless Steel

Tuning mechanical behavior and deformation mechanisms in high-manganese steels via carbon content modification

Effect of nitrogen content on microstructure, mechanical properties, and corrosion behaviour of coarse-grained heat-affected zone of nitrogen-containing austenitic stainless steel

Adding N to enhance low-cycle fatigue properties of high-Mn austenitic steel

The Role of Al/Ti in Precipitate-Strengthened and Austenite-Toughened Co-Free Maraging Stainless Steel

Advancement of strength and toughness in ultra-low carbon martensitic stainless steel by reversed austenite

Effect of Cr on the Microstructure and Strength‐Toughness of High‐Strength and Heat‐Resistant Stainless Steel

Nitrogen Effects in Additively Manufactured Martensitic Stainless Steels: Conventional Thermal Processing and Comparison with Wrought

Effect of Mn addition on microstructure and mechanical properties of GX40CrNiSi25-12 austenitic heat resistant steel

Effect of Nitrogen Content on Grain Refinement and Mechanical Properties of a Reversion-Treated Ni-Free 18Cr-12Mn Austenitic Stainless Steel

Enhancement of Yield Strength by Chromium/Nitrogen Alloying in High-Manganese Cryogenic Steel

Effects of Different Austenitizing Times on the Microstructure and Properties of Cr‐Ni‐Mo‐V Series High‐Strength Steels

The effect of Ti–Mo–Nb on the microstructures and tensile properties of a Fe–Mn–Al–C austenitic steel