Triboelectric Nanogenerator Driven Carbon Nanotube Cathode: A Sustainable Self-Powering Electron Source
Jiangtao Chen,Yu Dian Lim,Yun Zhao,Jianbiao Chen,Bingjun Yang,Zhiguo Wu,Yan Li
DOI: https://doi.org/10.1021/acsaelm.0c01029
IF: 4.494
2021-01-06
ACS Applied Electronic Materials
Abstract:A field electron emitter is a promising cold electron source that can be applied in various vacuum micro/nanoelectronic apparatus. On the other hand, triboelectric nanogenerators (TENGs) harvest mechanical energy from the surroundings and convert it into electricity. Due to the high voltage and current generation, TENGs can be employed as a pulsed mode voltage source to extract electrons from field electron emitters. Herein, we have prepared high-performance carbon nanotube (CNT) emitters, which show low turn-on field (2.29 V μm<sup>–1</sup>, for achieving the current density of 1.0 mA cm<sup>–2</sup>), high current density (115 mA cm<sup>–2</sup>@4.00 V μm<sup>–1</sup>), prolonged emission stability (without remarkable deterioration lasting for 18.5 h), and homogeneous emission patterns. Apart from that, the CNT emitter is assembled with contact-separation mode TENG. The TENG-driven CNT emitter shows a sustainable pulsed electron emission, which is justified by fluorescent image recording. The results imply the feasibility of self-powering field electron source by integrating highly efficient CNT cathode and high-voltage-output TENG. This paves the way to further realize the miniaturization, lightweight, safe, and cost-effectiveness of cold cathode-based vacuum electronic devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.0c01029?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.0c01029</a>.Schematic illustration of the measurement of the <i>V</i><sub>OC</sub> through resistors in a series (Figure S1); schematic of the setup of the field emission experimentation under TENG (Figure S2); SEM image of the CNT emitter (Figure S3); effect of the current emission densities on the applied voltages under different anode–cathode distances (Figure S4); typical field emission curves of CNT emitter recorded at different data-collecting intervals of 0.5, 0.8, 2, 5, and 30 s, the curves marked with various colors demonstrate different hysteresis trends (Figure S5); and single waveform of emission current under the influence of TENG (Figure S6) (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c01029/suppl_file/el0c01029_si_001.pdf">PDF</a>)Emission patterns of the CNT cathode under the influence of TENG (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c01029/suppl_file/el0c01029_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,engineering, electrical & electronic