Abstract:A simple spray approach to fabricate superhydrophobic coatings on tile and glass substrates is presented. Commercial available polyphenylene sulfide (PPS) and hydrophobic silica (H-SiO(2)) powder were suspended in ethanol and the mixed suspensions were spray on substrates. After dried at different temperatures, surface coatings with different hydrophobicity were obtained. By observing the surface morphologies with scanning electron microscope (SEM) and atomic force microscope (AFM), and measuring water contact angles with a contact angle system, factors affecting the morphology, roughness and contact angle of the surface coatings, such as thermal treatment temperature and the weight ratio of H-SiO(2) to PPS, were investigated in detail. With the increase of the thermal treatment temperature, both the surface roughness and the contact angle increased when the temperature was lower than 280 degrees C. As the weight ratio of H-SiO(2) to PPS rose from 1: 10 to 1:1, more H-SiO(2) powders accumulated on the surface, leading to a significant increase of hydrophobicity. The surface coating obtained at 280 degrees C with the weight ratio of H-SiO(2) to PPS 1:1 showed a water contact angle higher than 150 degrees and a sliding angle lower than 4, exhibiting fascinating superhydrophobic properties. The surface coating could remain superhydrophobicity upon a further increase in thermal treatment temperature or the amount of H-SiO(2) powder. Moreover, the surface coatings showed high contact angles, larger than 150, for all the solutions with pH ranging from 1 to 14. The abrasion resistant property of the as-prepared superhydrophobic surface coating was tested using a homemade setup. Being scraped by freely-falling sands, the superhydrophobic coating could keep its high hydrophobicity, while a commercial hydrophobic coating transformed from hydrophobicity to hydrophilicity. This result implied our superhydrophobic surface coating was very stable. Moreover, chalk powders on the superhydrophobic surface coatings could easily be washed off with water, indicating good self-cleaning properties. The presented approach is convenient and can be potentially applied in fabrication of superhydrophobic surfaces in large scale.

Superhydrophobic polymer composite coating on glass via spin coating technique

Durable self-cleaning nano-titanium dioxide superhydrophilic coating with anti-fog property

PREPARATION AND PROPERTIES OF SUPERHYDROPHOBIC POLYPHENYLENE SULFIDE COMPOSITE COATINGS

Production of an EP/PDMS/SA/AlZnO Coated Superhydrophobic Surface through an Aerosol-Assisted Chemical Vapor Deposition Process

Facile Fabrication of Superhydrophobic Nanocomposite Coatings Based on Water‐Based Emulsion Latex

Multifunctional and fluorine-free superhydrophobic composite coating based on PDMS modified MWCNTs/ZnO with self-cleaning, oil-water separation, and flame retardant properties

Superhydrophilic Smart Coating for Self-Cleaning Application on Glass Substrate

Transparent Superhydrophobic and Self-Cleaning Coating

Transparent and Durable SiO2‐containing Superhydrophobic Coatings on Glass

Low-cost preparation of durable, transparent, superhydrophobic coatings with excellent environmental stability and self-cleaning function

Transparent superhydrophilic composite coating with anti-fogging and self-cleaning properties

Fast Fabrication of Silicone-Modified Polyurethane/sio2 Composite Superhydrophobic Coating with Excellent Anti-Icing and Self-Cleaning Behaviour

A Facile Approach to UV-curable Super-Hydrophilic Polyacrylate Coating Film Grafted on Glass Substrate

Fabrication of silicone modified polyurethane matrix superhydrophobic coating with hydroxy-terminated polydimethylsiloxane modified SiO2 nanoparticles

Formation of Superhydrophobic Coatings Based on Dispersion Compositions of Hexyl Methacrylate Copolymers with Glycidyl Methacrylate and Silica Nanoparticles

Mechanically stable superhydrophobic coating of crosslinked polymer composite with self-healing ability

Enhancing glass surface hydrophobicity: the role of Perfluorooctyltriethoxysilane in advanced surface modification

Transparent Oil-Water Separating Spiky SiO2 Nanoparticle Supramolecular Polymer Superhydrophobic Coatings

Synthesis and self-cleaning properties of superamphiphobic coatings based on burr-like copolymer particles

Fabrication of TiO2 ̶ KH550 ̶ PEG Super-Hydrophilic Coating on Glass Surface without UV/Plasma Treatment for Self-Cleaning and Anti-Fogging Applications

Scalable preparation of efficiently self-healing and highly transparent omniphobic coating for glass