Effect of annealing treatment on texture evolution, microstructure and mechanical properties of an extruded Mg-Gd-Zn-Zr alloy
Nan Wang,Lei Xiao,Shifeng Luo,Guangyu Yang,Yan Wang,Xiaogang Fang,Jieming Chen,Hongwei Zhou,Wenjie Lu,Xinyu Yang,Jiuxing Zhang
DOI: https://doi.org/10.1016/j.jmrt.2023.10.249
IF: 6.267
2023-11-05
Journal of Materials Research and Technology
Abstract:Texture evolution, microstructure and mechanical properties of an extruded Mg-10Gd-1Zn-0.4Zr alloy during annealing were investigated. A bimodal microstructure containing coarse deformed grains and fine dynamically recrystallized grains is observed when the annealing temperature is lower than 200 °C. Many Mg 5 (Gd, Zn) phases are formed in the alloy annealed at 200 °C. Further upon increasing the annealing temperature, static recrystallization occurs and lamellar LPSO phase forms within the matrix. When the annealing temperature reaches 500 °C, an obvious grain growth is observed, and Zn 2 Zr 3 phases form. Meanwhile, the dominant texture component transforms from the basal texture ( parallel to extrusion direction) to an abnormal texture ( parallel to extrusion direction), which is attributed to the growth preference of the grains with abnormal texture. The alloy annealed at 200 °C possesses the optimal mechanical properties with the yield strength of 320 MPa, the ultimate strength of 368 MPa and elongation of 18.4 %. The contribution of each strengthening mechanism to the yield strength in annealed alloys is calculated quantitatively. Compared to the as-extruded alloy, the increment of the yield strength in the alloy annealed at 200 °C is mainly due to the increase in secondary phase strengthening, while the decrement of the yield strength in the alloy annealed at 500 °C is attributed to the reduction of grain boundary strengthening. This work sheds light on adjusting the texture and mechanical properties of the extruded Mg alloys via annealing treatment.
materials science, multidisciplinary,metallurgy & metallurgical engineering