Abstract:This investigation is aimed to study the dynamic failure behavior of 3-D braided carbon/epoxy composite by capturing the high-speed infrared image and simulating the temperature-rise response under high strain-rate compression. It is found that localized temperature rise is a good indication in damage and failure of the 3-D braided composite. Localized temperature can rise above a hundred degrees Celsius, reaching or even exceeding the Tg of the matrix resin and imperiling the polymer along damage regions in specimen. Temperature rise in localized paths of the specimens was caused by adiabatic shear along the boundaries of braided fibers or inside the fiber bundles. Sustaining decrease in stress after the peak strength is related to shear deformation, temperature rise and progressive damage. There is a correlation among localization of temperature rise, adiabatic shear band, resin softening, damages and failures in the 3-D braided carbon/epoxy composite under dynamic compression loading. For the out-of-plane compression, temperature always conducts from the broken interface to the inside of the fiber bundles along the radial, which will lead to the weakening of resin in fiber bundles. And damages, penetrating cracks and openings are verified with 'X'-shape localization of temperature rise. With the increase of strain rate, localization of temperature rise indicates that adiabatic shear bands begin to connect together to form larger and longer paths by the mutual shear effect among adjacent fiber bundles. For the in-plane compression, multi-cracks are found by observing the independent 'zigzag' shear bands converting to dependent 'zigzag' network. The temperature is easily localized at the crimp position of fiber bundle when they forming the 'zigzag' localization along the braiding paths of fiber bundles. However, some regions in 3-D braided carbon/epoxy composite have not experienced plastic shear deformation, which are isolated among 'zigzag' adiabatic shear network and their boundaries are the very paths for localized temperature rise.

High-speed infrared imaging and mesostructural analysis of localized temperature rise in damage and failure behavior of 3-D braided carbon/epoxy composite subjected to high strain-rate compression

Comparison of the in situ compressive behavior of carbon fibers woven ply laminates exposed to one‐sided heat flux: Thermoplastic versus thermosetting composites

X-ray microtomography analysis of the damage mechanisms in 3D circular braided carbon fiber/epoxy resin composite tubes under axial impact compression

High-Strain-Rate Compression Behavior and Failure Mechanism of 3d Mwk Carbon/Epoxy Composites

Effects of temperature and strain rate on impact compression behaviors of three-dimensional carbon fiber/epoxy braided composites

Temperature rise caused by adiabatic shear failure in 3D braided composite tube subjected to axial impact compression

Experimental study on the fabrication, high-temperature properties and failure analysis of 3D seven-directional braided composites under compression

Numerical analyses on thermal stress distribution induced from impact compression in 3D carbon fiber/epoxy braided composite materials

Strain Rate and Temperature Effect on Mechanical Properties and Failure of 3D Needle-Punched Carbon/Carbon Composites under Dynamic Loading

Experimental and numerical study of in-plane compressive properties and failure of 3D six-directional braided composites with large braiding angle

High-fidelity prediction and temperature-rise mechanism for low-velocity impact of triaxially braided composites

Transverse impacts‐induced deformation and damage of 3D angle‐interlock woven composites at elevated temperatures

Internal shear damage evolution of CFRP laminates ranging from -100°C to 100°C using in-situ X-ray computed tomography

Elevated temperature effect on tension fatigue behavior and failure mechanism of carbon/epoxy 3D angle-interlock woven composites

Analysis of in-plane compression failure mechanism in carbon fiber braided composite with different off-axial angles

Effects of high temperature and strain rate on the impact-induced inter-laminar shear behavior of plain woven CF/PEEK thermoplastic composites

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

On the tensile properties and failure mechanisms of 3D six-directional braided composites at elevated temperatures

The temperature effect on the inter-laminar shear properties and failure mechanism of 3D orthogonal woven composites

A hierarchical multiscale model for the elastic-plastic damage behavior of 3D braided composites at high temperature