Abstract:This study represents the first scientific effort to evaluate the technical feasibility of rice husk ashes (RHA; ash burned after RH) as a new water treatment material for adsorption of Sb(III) from drinking water. Three RHA samples (RHA300, RHA450, RHA600) were prepared from RH at 300, 450 and 600 degrees C, respectively. Compared with RH, RHA had great specific surface areas, small particle sizes, and large total pore volumes. Moreover, the RHA was characterized by an amorphous structure. In the subsequent bench-scale tests, the RHA samples were utilized to adsorb Sb(III) from water. Kinetics tests showed that pseudo first-order and pseudo second-order kinetics models both well fit the experimental data, and Sb(III) sorption rates followed the order of RHA450 > RHA600 > RHA300 > RH. Among the 4 tested adsorption isotherm models (Freundlich, Langmuir, Temkin, and Dubinin-Radushkevich), the Langmuir isotherm was the best one to fit the measured data, and the adsorption capacities of RHA300, RHA450 and RHA600 were 1.407, 3.842 and 2.731 mg/g, respectively. Solution pH, natural organic matters (NOMs) and certain cations (e.g. Fe3+ and Fe2+) were significant factors controlling the adsorption process. RHA300 adsorption was increased with increasing pH from 2 to 12, while RHA450 and RHA600 showed a high adsorption potential at pHs 4-10. Their maximum adsorption capacities were observed at pH values where the lowest zeta potentials were found. Fe3+ and Fe2+ both greatly inhibited RHA adsorption of Sb(III). In contrast, K+, Na+, Mn2+ and Cu2+, as well as humic acid (HA) (the major NOM fraction), had a minor impact upon the adsorption. Our results demonstrate that RHA is a technically effective sorbent to address the Sb(III) pollution in water.

Recovery of silica and carbon black from rice husk ash disposed from a biomass power plant by precipitation method

Beneficial Utilization of Rice Husk Ash (rha) As A New Sorbent for Removal of Antimony (iii) from Water

PREPARATION OF HIGH-PURITY WHITE CARBON BLACK BY RICE HUSK ASH FROM BIOMASS POWER PLANT

Extraction of Silica from Rice Husk 71

Silica precipitation from rice husk ash leachate: optimization and kinetic analysis

Production and characterization of silica materials from rice husk ash by different combustion processes

Experimental Study on Preparation of Amorphous SiO2 by Fluidized Bed Combstion of Rice Husk

Preparation of highly dispersed nanosilica from rice husk by aprecipitation method combined with high pressure homogenization

Mechano-chemical conversion of rice husk ash and gasifier-derived rice husk ash into porous silicon

Preparation of Silica by Alkaline-Heating and Precipitation Method from Corn Straw Ash

Sustainable utilization of rice husk waste for preparation of ordered nanostructured mesoporous silica and mesoporous carbon: Characterization and adsorption performance

Influence of pre-treatment processes on the purity and characteristics of silica extracted from rice husk

Simultaneous Synthesis of Silica Polymorphs and Activated Carbon from Rice Husk

Preparation of Precipitated Nano-silica from Acid Leaching Residue of Coal Ash by Carbonation Method

Study on preparation and surface modification of precipitated silica obtained from fly ash

Kinetic study on the preparation of silica from rice husk under various pretreatments

Recycling of carbonized rice husk for producing high purity silicon by the combination of electric arc smelting and slag refining

Coproduction of silicon nitride & oxynitride whiskers and precipitated silica from industrial rice husk ash

High temperature capture of CO2 on lithium-based sorbents from rice husk ash

Extraction of Aluminum Hydroxide from Coal Fly Ash by Pre-Desilication and Calcination Methods