Abstract:The aim of this study was to investigate the physical, mechanical, morphological, structural, and thermal properties of polylactic acid (PLA) and polyhydroxybutyrate (PHB) biopolymer composites reinforced with thermally treated wood flour and to determine the formulations having optimum properties by using multi-criteria decision-making (MCDM) methods. As a filler, Scots pine wood flour (untreated and thermally treated at 212 °C) was used at the loading rates of 10% and 30%. The samples were prepared using a twin-screw extruder and then by compression molding. The results showed that the addition of both thermally treated and untreated wood flour slightly increased the density of the composites. According to the color measurement, the thermally treated wood composites were slightly darkened in appearance. In the composites, with both wood fillers, the water absorption and thickness swelling ratios had increased during the 20–250 days of water exposure. Lower water absorption and thickness swelling rates were found for the composites with thermally treated wood filler compared to the other composites. The wood fillers generally lowered the mechanical properties of the PLA and PLA/PHB composites, with the PHB composites as the exception. However, the tensile modulus and Izod impact strength of the composites generally increased with the addition of wood fillers. Morphological examination performed by scanning electron microscopy (SEM) indicated that the wood flour was mostly homogeneously distributed in the matrix, which improved the mechanical properties of the composites. Thermogravimetric analysis (TGA) showed that the addition of wood filler to the neat biopolymers as a rule did not provide significant improvement in the thermal stability; however, the fillers increased the thermal stability of neat PHB. The Fourier-transform infrared (FTIR) spectroscopy detected no differences in the chemical structure of the composites. The X-ray diffraction (XRD) results indicated a general increase in the crystallinity with the addition of wood fillers to the neat biopolymers and the blends. All the findings were subjected to MCDM analysis to determine the formulation having the optimum properties and the results showed this to be the neat PLA sample.

Correlation between physical bonding and mechanical properties of wood–plastic composites: part 2: effect of thermodynamic factors on interfacial bonding at wood–polymer interface

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Investigating the influence of fabrication parameters, flax fibre reinforcement, and ageing on interlaminar shear strength in thermoplastic-bonded wood veneers

Effect of Matrix–Particle Interfacial Adhesion on the Mechanical Properties of Poly(lactic acid)/Wood-Flour Micro-Composites

Transforming interface properties of wood laminate composites functionalized by adhesive penetration

STRUCTURAL ASSESSMENT OF LAMINATED WOOD VENEER/PLASTIC SHEET COMPOSITES USED AS BUILDING MATERIAL

Role of Maleated Coupling Agents on the Interface Adhesion of Polypropylene—Wood Composites

Effects of wood fiber surface chemistry on strength of wood–plastic composites

Qualification Of Adhesives For Bonding Wood To Fiber-Reinforced Plastics

Effects of manufacturing parameters on mechanical interface properties of thin wood veneer laminates

Effects Of Coupling Agent And Interfacial Modifiers On Mechanical Properties Of Poly(Lactic Acid) And Wood Flour Biocomposites

The use of wood veneer to beautify wood plastic composites

The role of wood extractives in structural hardwood bonding and their influence on different adhesive systems

Interfacial adhesion mechanisms of ultra-highly filled wood fiber/polyethylene composites using maleic anhydride grafted polyethylene as a compatibilizer

Fiber-Reinforced Composite and Wood Bonded Interfaces: Part 1. Durability and Shear Strength

Influence of wood extractives on two-component polyurethane adhesive for structural hardwood bonding

Environmental effects on the bond at the interface between FRP and wood

Improving interfacial bonding strength between epoxy and PE-based wood plastic composites by micro-riveting

Understanding the impact of wood type and moisture on the bonding strength of glued wood

Amide wax-assisted interfacial compatibilization of maleic anhydride-grafted polyethylene for high-performance wood-plastic composites

Performance Characterization Of Wood Composites Reinforced With Frp