Revealing the intrinsic nature of Cu- and Ce-doped Mn 3 O 4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS
Zihao Hu,Xiaoying Zhou,Tiantian Zhang,Zuliang Wu,Jing Li,Wei Wang,Erhao Gao,Jiali Zhu,Shuiliang Yao
DOI: https://doi.org/10.1039/d4dt02391a
IF: 4
2024-10-03
Dalton Transactions
Abstract:Aiming at the problem of the poor performance of an Mn-MOF-74-derived Mn 3 O 4 catalyst in low-temperature carbon monoxide (CO) oxidation, copper (Cu) and cerium (Ce) elements were used to modify the Mn 3 O 4 catalyst to improve its performance in low-temperature CO oxidation. According to the results of catalytic performance testing, the CO oxidation activity of the Cu 0.3 Mn 2.7 O 4 catalyst was significantly improved compared with that of the pristine Mn 3 O 4 catalyst, when a CO conversion rate of 90% was achieved at 118 °C. According to X-ray photoelectron spectroscopy and Brunauer–Emmett–Teller analyses, the (Mn 2+ + Mn 3+ )/(Mn 2+ + Mn 3+ + Mn 4+ ) ratio and the O ads /O total ratio increased after Cu doping, indicating promoted oxygen vacancy generation. In addition, the increased specific surface area was beneficial for the adsorption of reactant molecules and the exposure of active sites. According to H 2 -temperature-programmed reduction characterization, Cu doping significantly enhanced the performance of the Cu 0.3 Mn 2.7 O 4 catalyst during low-temperature redox. Finally, these factors synergistically promoted the degradation of CO over the Cu 0.3 Mn 2.7 O 4 catalyst. In addition, operando diffuse reflectance Fourier transform infrared spectroscopy results suggested the presence of more terminal-type oxygen, which is essential for the catalytic oxidation of CO on the surface of the Cu 0.3 Mn 2.7 O 4 catalyst. Moreover, the Cu 0.3 Mn 2.7 O 4 catalyst also showed excellent resistance to carbonate, and remarkable stability.
chemistry, inorganic & nuclear