Enhanced adsorption performance and governing mechanisms of ball-milled biochar for the removal of volatile organic compounds (VOCs)

Wei Xiang,Xueyang Zhang,Kuiqing Chen,June Fang,Feng He,Xin Hu,Daniel C.W. Tsang,Yong Sik Ok,Bin Gao

DOI: https://doi.org/10.1016/j.cej.2019.123842

IF: 15.1

2020-04-01

Chemical Engineering Journal

Abstract:Hickory wood was pyrolyzed at 300 °C, 450 °C, and 600 °C to produce biochars, which were then modified by ball milling. The pristine and ball-milled biochars were used to remove volatile organic compounds (VOCs) including acetone, ethanol, chloroform, cyclohexane, and toluene. Compared with the corresponding pristine one, each ball-milled biochar showed significantly improved structural characteristics. Their specific surface area (SSA) increased by 1.4–29.1 times, average pore size (APS) decreased slightly, and the hydrophilicity and polarity were also enhanced according to the elemental analysis. The adsorption of VOCs by ball-milled biochar increased by 1.3–13.0 folds, and the maximum adsorption capacity of acetone was up to 103.4 mg/g. The adsorption of polar VOCs (acetone, ethanol, and chloroform) onto ball-milled biochars was mainly controlled by surface adsorption process, which was affected by the SSA, APS, and volatile organic matter of the biochars, as well as the properties of the VOCs. The adsorbed VOCs were completely desorbed from the ball-milled biochars at relatively low temperature (≤115.2 °C). Reusability experiments with five adsorption-desorption cycles showed that ball-milled biochar had an excellent reusability for all VOCs. Ball-milled biochars can therefore be used as an effective and regenerable adsorbent for the removal of VOCs.

engineering, chemical, environmental

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the adsorption performance of biochar for volatile organic compounds (VOCs) and its control mechanism through ball - milling modification of biochar. Specifically, the researchers ball - milled biochar (HW300, HW450, HW600) prepared at different temperatures in order to improve the adsorption capacity of these biochar for five representative VOCs (acetone, ethanol, chloroform, cyclohexane, toluene). The main objectives of the study include:

1. **Production and Characterization**: Prepare the original biochar and ball - milled biochar, and characterize their structural properties, such as specific surface area (SSA), average pore size (APS), surface functional groups, etc.
2. **Analysis of Adsorption Performance**: Evaluate the adsorption performance of the original biochar and ball - milled biochar for different VOCs.
3. **Analysis of Adsorption Mechanism**: Explore the adsorption mechanism of VOCs on ball - milled biochar, especially the surface adsorption process and its influencing factors.
4. **Evaluation of Regenerability**: Evaluate the regenerative performance of ball - milled biochar through multiple adsorption - desorption cycle experiments.

The study found that ball - milling treatment significantly increased the specific surface area and surface polarity of biochar, thereby significantly enhancing its adsorption capacity for VOCs. In addition, the adsorption of VOCs on ball - milled biochar is mainly controlled by the surface adsorption mechanism, and all adsorbed VOCs can be completely desorbed at a relatively low temperature, showing good regenerative performance. Therefore, ball - milled biochar can be used as an efficient and renewable adsorbent for the removal of VOCs.