Abstract:CoMoCrSi coatings with different thickness were prepared by high velocity oxy-fuel spraying (HVOF) and atmospheric plasma spraying (APS), respectively. Variation of microstructure and phase constitution the coatings were investigated by SEM and XRD, respectively. Thermal shock performance of the coatings was evaluated by heating (500 °C and 900 °C) and water quenching method. Compared with APS coatings, the as-sprayed HVOF coatings exhibited denser microstructure and higher hardness. The phase and microstructure of the coatings did not change significantly after 50 thermal cycles at 500 °C. On the contrary, spallation was observed in APS coatings with thickness of ∼350 μm during 900 °C thermal shock cycles. Obvious oxidation appeared in all of the coatings after 900 °C thermal shock. Meanwhile, segmentation cracks perpendicular to the coating surface were found in the edge of 900 °C thermal shocked HVOF coatings (both ∼350 μm and ∼130 μm) and APS coatings (∼350 μm). Element interdiffusion was not detected between the substrate and coating after 50 thermal shocks at 900 °C or 500 °C. After the thermal shock at 500 °C, the microhardness of the ∼130 μm coating did not change greatly while the microhardness of the ∼350 μm coating was greatly improved. After the thermal shock at 900 °C, the microhardness of the coating increased by about 40 % due to the reduction of defects in the coating and the generation of hard phases. At the same time, the migration of elements and the oxidation and recrystallization of some phases may increase the hardness of the coating.

CoMoCrSi coatings prepared by high-velocity oxygen fuel spraying: microstructure and mechanical properties at elevated temperatures up to 800 °C

Fabrication and effect of heat treatment on the microstructure and tribology properties of HVOF-sprayed CoMoCrSi coating

Microstructure and thermal shock behavior of CoMoCrSi coatings prepared by HVOF and APS

Investigating the Effects of CoMoCrSi Powder Composition and Particle Size, and Annealing Heat Treatment on Microstructure and Mechanical and Tribological Performance of HVOF Sprayed Coatings

A Novel Oxide Layer Formed on the 800 °C-Annealed CoMoCrSi Coating Significantly Reduced Friction and Wear at Room Temperature

Microstructure of HVOF-sprayed Ag–BaF2⋅CaF2–Cr3C2–NiCr coating and its tribological behavior in a wide temperature range (25 °C to 800 °C)

High temperature induced “glaze” layer formed in HVOF-sprayed NiCrWMoCuCBFe coating and its wear reduction mechanism

High-temperature tribological property of Fe-based amorphous alloy coating

Microstructure and Corrosive Wear Properties of CoCrFeNiMn High-Entropy Alloy Coatings

Microstructure and mechanical property of high velocity oxy-fuel sprayed WC-Cr3C2-Ni coatings

Influence of Spray Parameters on Sliding Wear Properties of HVOF Sprayed Fe-Based Amorphous Coatings

Preparation and Properties of Ultra-High Hardness Co-Cr-Mo-Nb-B High-Temperature Amorphous Alloy Coating

The influence of nano-CeO2 on tribological properties and microstructure evolution of Cr3C2-NiCrCoMo composite coatings at high temperature

Influence of microwave hybrid heating on the sliding wear behaviour of HVOF sprayed CoMoCrSi coating

Effect of Nano-ZrO2 on the Microstructure and High Temperature Tribological Properties of MoSi2 Coating

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

High-temperature tribological behavior of thermally-treated supersonic plasma sprayed Cr3C2-NiCr coatings

Room-Temperature and High-Temperature Wear Behaviors of As-Sprayed and Annealed Cr3C2-25NiCr Coatings Prepared by High Velocity Air-Fuel Spraying

Thermal-mechanical driven oxidation of NiCr-Cr3C2-BaF2/CaF2 composite coating at high temperature

Preparation and tribological properties of NiCr–Mo–Ag–O/Mo–V–Ag–O bilayer film at RT-1000 °C

Tribological behavior of HVOF carbon coating for wear resistance applications