Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

High-Capacity Hard Carbon Synthesized from Macroporous Phenolic Resin for Sodium-Ion and Potassium-Ion Battery

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Studies on electrochemical sodium storage into hard carbons with binder-free monolithic electrodes

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

From Micropores to Ultra-micropores inside Hard Carbon: Toward Enhanced Capacity in Room-/Low-Temperature Sodium-Ion Storage

High-Capacity Hard Carbons Enabled by a Sodium Carborane Solid Electrolyte for Sodium-Ion Batteries

MgO‐Template Synthesis of Extremely High Capacity Hard Carbon for Na‐Ion Battery

3D connected porous structure hard carbon derived from paulownia xylem for high rate performance sodium ion battery anode

Hard Carbon Microsphere with Expanded Graphitic Interlayers Derived from a Highly Branched Polymer Network as Ultrahigh Performance Anode for Practical Sodium-Ion Batteries

A N/S/O-tridoped hard carbon network anode from mercaptan/polyurethane-acrylate resin for potassium-ion batteries

Impact of Hard Carbon Properties on Their Performance in Potassium-Ion Batteries

Epoxy phenol novolac resin: A novel precursor to construct high performance hard carbon anode toward enhanced sodium-ion batteries

Investigating The Superior Performance of Hard Carbon Anodes in Sodium‐Ion Compared with lithium‐ and potassium‐Ion Batteries

New Template Synthesis of Anomalously Large Capacity Hard Carbon for Na‐ and K‐Ion Batteries

Pore Structure Regulation of Hard Carbon: Towards Fast and High-Capacity Sodium-Ion Storage

Correlation between Potassium-Ion Storage Mechanism and Local Structural Evolution in Hard Carbon Materials

Hard carbon microspheres derived from resorcinol formaldehyde resin as high-performance anode materials for sodium-ion battery

Intrinsically Nitrogen-Enriched Biomass-Derived Hard Carbon with Enhanced Performance as a Sodium-Ion Battery Anode

Scalable synthesis of N/S co-doped hard carbon microspheres as a high-performance anode material for sodium-ion batteries

Exploring Carbonization Temperature to Create Closed Pores for Hard Carbon As High-Performance Sodium-Ion Battery Anodes

Hard carbon with an opened pore structure for enhanced sodium storage performance