Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

MgO‐Template Synthesis of Extremely High Capacity Hard Carbon for Na‐Ion Battery

New Template Synthesis of Anomalously Large Capacity Hard Carbon for Na‐ and K‐Ion Batteries

Tuning Nanopore Structure of Hard Carbon Anodes by Zinc Gluconate for High Capacity Sodium Ion Batteries

Ion-Catalyzed Synthesis of Microporous Hard Carbon Embedded with Expanded Nanographite for Enhanced Lithium/Sodium Storage

High-Capacity Hard Carbons Enabled by a Sodium Carborane Solid Electrolyte for Sodium-Ion Batteries

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

From Micropores to Ultra-micropores inside Hard Carbon: Toward Enhanced Capacity in Room-/Low-Temperature Sodium-Ion Storage

High-Performance Sodium-Ion Batteries Based on Nitrogen-Doped Mesoporous Carbon Spheres with Ultrathin Nanosheets.

High-Capacity Hard Carbon Synthesized from Macroporous Phenolic Resin for Sodium-Ion and Potassium-Ion Battery

Studies on electrochemical sodium storage into hard carbons with binder-free monolithic electrodes

Ultrafast synthesis of hard carbon for high-rate and low-temperature sodium-ion storage through flash Joule heating

Ultrahigh Plateau‐Capacity Sodium Storage by Plugging Open Pores

Developing an oxygen-induced capacitive hard carbon anode for fast sodium ion storage through pore-scale engineering

Hierarchically Porous Hard Carbon with Graphite Nanocrystals for High-Rate Sodium Ion Batteries with Improved Initial Coulombic Efficiency

MgO-template Synthesis of Hollow N/O Dual Doped Carbon Boxes as Extremely Stable Anode for Potassium Ion Batteries

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Pore Structure Regulation of Hard Carbon: Towards Fast and High-Capacity Sodium-Ion Storage

Hard Carbon/graphene Microfibers As a Superior Anode Material for Sodium-Ion Batteries

Tailored Regulation of Graphite Microcrystals via Tandem Catalytic Carbonization for Enhanced Electrochemical Performance of Hard Carbon in the Low‐Voltage Plateau

Tailoring Pseudo-Graphitic Domain by Molybdenum Modification to Boost Sodium Storage Capacity and Durability for Hard Carbon

Gelatin‐Derived Hard Carbon Achieves Effective Control of Microstructure toward Fast and Durable Sodium Storage