A lithium–aluminosilicate zeolite membrane for separation of CO2 from simulated blast furnace gas

Priyanka Roy,Nandini Das

DOI: https://doi.org/10.1007/s10934-019-00849-0

2020-01-10

Journal of Porous Materials

Abstract:In this study, for the first time, the small pore size (0.28 × 0.37 nm) Li–aluminosilicate zeolite membrane was synthesized for separation of CO₂ from H₂–CO₂ and H₂–CO₂–N₂–CO (simulated blast furnace gas) gas mixtures. Li–aluminosilicate membranes were prepared on porous clay alumina tubes by sonication mediated hydrothermal method using pre synthesized zeolite powders as seeds. The zeolite formation was confirmed by X-ray diffraction pattern and FESEM analysis. The scanning electron micrograph of the membrane, suggested the uniformity of the dense structure of the membrane. Single-gas and mixed-gas permeation experiments through membranes were carried out at 25 °C using H₂, CO₂ and N₂ single-component gases and mixture of H₂–CO₂, H₂–CO₂–N₂–CO for simulated blast furnace gas composition. Synthesized Li–aluminosilicate zeolite shows appreciable CO₂ adsorption capacity at liquid nitrogen temperature compared with other reported zeolites. In case of single gas permeation, membrane shows usual pattern of permeation. For mixture gas, separation efficiency of Li–zeolite membrane increased abruptly compared to the other zeolite membranes. The maximum CO₂–H₂, CO₂–N₂ and CO₂–CO separation selectivities were found to be 78, 8.7 and 67.3 respectively, with permeance of H₂, CO₂ and N₂ 2.21 × 10⁻⁷, 1.01 × 10⁻⁷ and 0.8 × 10⁻⁷ mol m⁻² s⁻¹ Pa⁻¹ at 25 °C respectively.

materials science, multidisciplinary,chemistry, physical, applied