Conductive textiles prepared by spray coating of water-based graphene dispersions

Archana Samanta,Romain Bordes

DOI: https://doi.org/10.1039/c9ra09164e

IF: 4.036

2020-01-01

RSC Advances

Abstract:Effect of coating technique on surface properties and conductivity of PET textiles.

chemistry, multidisciplinary

What problem does this paper attempt to address?

Effects of three fabric weave textures on the electrochemical and electrical properties of reduced graphene/textile flexible electrodes

Wei Wang,Tao Li,Kang Liu,Shuo Wang,Huaxin Peng

DOI: https://doi.org/10.1039/c9ra08524f

IF: 4.036

2020-01-01

RSC Advances

Abstract:Textile textures formed through woven, knitted or nonwoven weaving technology have critical effects on the electrical and electrochemical properties of flexible electrodes. Therefore, the effects of textile structures, including porosity and pore configuration, on the loading amount of reduction graphene (RGO), the electrical and electrochemical properties were systematically studied. The results show that knitted fabric had the highest mass loading of RGO sheets and lowest sheet resistance among these three fabrics. However, the specific capacitance of woven fabric was optimum 40.5 F g(-1) at a scan rate of 5 mV s(-1) within the voltage window of 0-0.8 V, which was ascribed to its suitable porosity and pore size firmly anchoring the RGO sheets. Also, the RGO/woven cotton electrodes exhibited good cycling stability and excellent electrochemical stability without an obvious loss in the capacitive performance. The above results provide a theoretical basis for the selection of textile substrates for high-performance flexible electrodes.
PET/Graphene Nanocomposite Fibers Obtained by Dry-Jet Wet-Spinning for Conductive Textiles

Laia León-Boigues,Araceli Flores,Marian A. Gómez-Fatou,Juan F. Vega,Gary J. Ellis,Horacio J. Salavagione

DOI: https://doi.org/10.3390/polym15051245

IF: 5

2023-03-02

Polymers

Abstract:The combination of polyethylene terephthalate (PET), one of the most used polymers in the textile industry, with graphene, one of the most outstanding conductive materials in recent years, represents a promising strategy for the preparation of conductive textiles. This study focuses on the preparation of mechanically stable and conductive polymer textiles and describes the preparation of PET/graphene fibers by the dry-jet wet-spinning method from nanocomposite solutions in trifluoroacetic acid. Nanoindentation results show that the addition of a small amount of graphene (2 wt.%) to the glassy PET fibers produces a significant modulus and hardness enhancement (»10%) that can be partly attributed to the intrinsic mechanical properties of graphene but also to the promotion of crystallinity. Higher graphene loadings up to 5 wt.% are found to produce additional mechanical improvements up to »20% that can be merely attributed to the superior properties of the filler. Moreover, the nanocomposite fibers display an electrical conductivity percolation threshold over 2 wt.% approaching »0.2 S/cm for the largest graphene loading. Finally, bending tests on the nanocomposite fibers show that the good electrical conductivity can be preserved under cyclic mechanical loading.

polymer science
Developing Graphene‐based Conductive Textiles Using Different Coating Methods

Babak Abdi,Ali Tarhini,Hossein Baniasadi,Ali R. Tehrani‐Bagha

DOI: https://doi.org/10.1002/admt.202301492

IF: 6.8

2024-01-04

Advanced Materials Technologies

Abstract:Abstract In this research, a series of graphene‐based conductive textiles is developed by three different coating methods, including dip‐coating (D), airbrushing (A), and filtration (F). The cellulose substrate consists of a blend of cotton and rayon fabric, and the coating formulation is based on a mixture of graphene powder as a conductive filler, polyurethane (PU) as a binder, and poly(vinylidene fluoride‐co‐hexafluoropropylene) (PVDF‐HFP) as a thermoplastic co‐binder. The thermogravimetric analysis (TGA) results are used to prove an enhancement in the thermal stability of the coated fabrics. The graphene content of the coated samples is also estimated from the char residue at 800 °C of the TGA profiles. The graphene‐based coating converts the water‐adsorbing cellulose fabric to a hydrophobic surface as the water contact angle raises from 0° to more than 107° after coating. The mechanical properties of the plain cellulose fabric enhance considerably in terms of tensile strength and tensile modulus, where the highest improvement is seen in the Dip‐coating method, with an 89% increase in tensile strength compared to cellulose fabric. The graphene‐based coating developed in this work enhances the physical, thermal, mechanical, and conductivity properties of the plain cellulose substrate. The resulting coated fabrics can be potentially used in wearable smart electronic textiles.

materials science, multidisciplinary
Preparation and characterization of high-performance water-based graphene dispersions for conductive coating on textiles

Sena Çaylak,Onur Demirel,Majid Javadzadehkalkhoran,Amir Navidfar,Merve Yaşacan,Levent Trabzon

DOI: https://doi.org/10.1080/00405000.2024.2343117

IF: 1.7698

2024-04-19

Journal of the Textile Institute

Abstract:Studies on e-textile applications have gained momentum with advanced material technologies. Graphene derivatives have become the focus of e-textile advanced studies due to their high conductivity potential. The chemical selection while preparing graphene dispersions to functionalize textiles affects the dispersion quality and integration into the fabric. In this study, water-based green graphene dispersions were prepared using sodium dodecyl benzene sulfonate (SDBS) as a surfactant and polyvinyl alcohol (PVA) as a binder due to its high solubility in water. The stability of graphene nanoplatelets (GNP), GNP/SDBS and GNP/SDBS/PVA dispersions were examined with the naked eye at certain time intervals. UV–vis spectroscopy results indicated that SDBS provided better dispersion and stability of graphene. The XPS results showed a strong interaction between GNP and SDBS, while the binding of PVA and SDBS in the dispersion was supported by FTIR results. Overall, the dispersion quality of water-based graphene dispersion was enhanced using PVA and SDBS for e-textile application. The electrical conductivity and tensile strength of the graphene-coated fabrics increased up to ∼1.6 (MΩ/☐) and 388%, respectively, in compared to the intact fabric.

materials science, textiles
The Influence of Substrate Functionalization for Enhancing the Interfacial Bonding between Graphene Oxide and Nonwoven Polyester

Junaid Khan,M. Mariatti

DOI: https://doi.org/10.1007/s12221-021-1386-y

IF: 2.5

2021-06-09

Fibers and Polymers

Abstract:Electronic textiles or e-textiles have become a hot topic considering the future era of wearable electronics that are expected to replace currently available non-flexible devices. Among various methods, coating carbon-based conductive fillers on the flexible fibrous surface seems to be a promising method for e-textile and many other applications. Graphene is the top candidate among other carbon forms owing to its exceptional properties and nontoxicity. The functional groups present on the fibers surface has a significant impact on the adhesion and bonding of graphene sheets, which in turn have a profound effect on forming conductive networks that lead to improved performance of the end product. In this article, graphene oxide (GO) is coated on unmodified and chemically surface modified with positively (amine) and negatively surface (alkali) charged polyester non-woven fabrics. The facile dip-coating technique was used to coat the fabrics, surface bonding, morphology, wettability, and thermal properties of the modified surfaces were thoroughly investigated. The study revealed that modification of the fibre surface leads to increased coating uptake, improved thermal properties and uniform coating coverage. The polyester modified with sodium hydroxide exhibited the best result with an improvement of 30 % for uptake and 15 % for thermal conductivity as compared with the untreated polyester demonstrating the importance of functional groups on the surface of the fibers.

materials science, textiles,polymer science
Elaboration of a Conductive Textile by Coating for Clothes Equipped with Fourth-Generation Photovoltaic Cells

Jaouani H,Saifaoui D,Dalal M

DOI: https://doi.org/10.4172/2165-8064.1000357

2018-01-01

Abstract:Conducting polymer coated in textiles possess a wide range of electrical properties. The surface resistivity is influenced by concentrations of the reactants, thickness of the coating, nature of the substrate surface, extent of penetration of the polymer into the textile structure and the strength of the binding of the coating to the textile surface. Low resistivity in fabric results from highly doped thicker coatings that penetrate well into the textile structure thus enabling good electrical contact between fibers. In this study, we had chosen copper as conductor polymer for coating. The electrical conductivity is influenced by the thickness of coating paste, the nature of the substrate surface. The thickness of the paste and the concentration of the copper were studied in this paper. Furthermore, the electrical surface resistance decreased from 68 MΩ to 8 MΩ with decreasing in coating thickness. However, the thickness of coated fabric is very important factor to determine conductivity and application of textile. In addition, we had noticed that the airflow is affected by the coating thickness which the penetration of the airflow differs from the lower thickness to the higher one. This study confirm that we can use coating woven fabric to develop a textile substrate responding to characteristics such as electrical resistance, drapability, air permeability and tensile strength, which are particularly important to be used as a support for flexible photovoltaic cells in clothes.
Surface Characterization and Electrical Properties of Spin- Coated Graphene Conductive Film

Weijun Zhang,Ming Li,Liming Gao,Xiaolei Ban

DOI: https://doi.org/10.1109/icept.2015.7236544

2015-01-01

Abstract:The Excellent printability of graphene sheets on large scale, flexible substrates makes graphene a perfect substitute of traditional conductive material in electronics industry. In this letter we demonstrate several properties of conductive film prepared by spin-coating graphene on PET substrates. After spin coating and air dry, the graphene film had a sheet resistance of 47.4Ω/□, resistivity of 1.07 mΩ·m. With a subsequent heating at 70°C, the resistivity was reduced to 0.18mΩ·m due to more outgassed liquidous solution and better contact of graphene nanoplatelet. Multilayer films were also prepared, and the graphene resistivity and microstructure versus film thickness was investigated. It is observed that the electric resistance declines as the film thickness increases. The thick film resulted in less-rough surface according to Scanning Electronic Microscope (SEM) and Atomic Force Microscope (AFM) inspection.
A Facile Approach of Fabricating Electrically Conductive Knitted Fabrics Using Graphene Oxide and Textile-Based Waste Material

Abdullah Al Faruque,Alper Kiziltas,Deborah Mielewski,Maryam Naebe,Md Abdullah Al Faruque

DOI: https://doi.org/10.3390/polym13173003

IF: 5

2021-09-04

Polymers

Abstract:This research investigated a feasible approach to fabricating electrically conductive knitted fabrics using previously wet-spun wool/polyacrylonitrile (PAN) composite fibre. In the production of the composite fibre, waste wool fibres and PAN were used, whereby both the control PAN (100% PAN) and wool/PAN composite fibres (25% wool) were knitted into fabrics. The knitted fabrics were coated with graphene oxide (GO) using the brushing and drying technique and then chemically reduced using hydrazine to introduce the electrical conductivity. The morphological study showed the presence of GO sheets wrinkles on the coated fabrics and their absence on reduced fabrics, which supports successful coating and a reduction of GO. This was further confirmed by the colour change properties of the fabrics. The colour strength (K/S) of the reduced control PAN and wool/PAN fabrics increased by ~410% and ~270%, and the lightness (L*) decreased ~65% and ~71%, respectively, compared to their pristine fabrics. The Fourier transform infrared spectroscopy showed the presence and absence of the GO functional groups along with the PAN and amide groups in the GO-coated and reduced fabrics. Similarly, the X-ray diffraction analysis exhibited a typical 2θ peak at 100 that represents the existence of GO, which was demolished after the reduction process. Moreover, the wool/PAN/reduced GO knitted fabrics showed higher electrical conductivity (~1.67 S/cm) compared to the control PAN/reduced GO knitted fabrics (~0.35 S/cm). This study shows the potential of fabricating electrically conductive fabrics using waste wool fibres and graphene that can be used in different application fields.

polymer science
Electrically conductive textile coating with a PEDOT-PSS dispersion and a polyurethane binder

Maria Åkerfeldt,Martin Strååt,Pernilla Walkenström

DOI: https://doi.org/10.1177/0040517512444330

IF: 2.3

2012-11-27

Textile Research Journal

Abstract:Electrically conductive textile coatings have been prepared by the addition of a dispersion of poly(3,4-ethylenedioxythiophene)-polystyrene sulfonate (PEDOT-PSS) and ethylene glycol to a polyurethane-based coating formulation. The formulations were designed to have similar viscosities, measured with a rheometer using a cone-and-plate set-up. The formulations were applied to woven poly(ethylene) terephthalate substrates using a direct coating method. The concentration PEDOT-PSS in the finished coatings varied between 0.7 and 6.2 wt%, the coating deposit between 19 and 155 g/m 2 and the drying procedure between 4 hours at 20°C and 10 minutes at 150°C. Surface resistivity was measured with a ring probe and surface topology was addressed with scanning electron microscopy (SEM). The PEDOT-PSS concentration had a large effect on the resistivity, which dropped by five orders of magnitude with an increased concentration. The steepest decrease occurred between 1 and 3 wt% PEDOT-PSS, indicating a percolation threshold. An increased coating deposit resulted in a resistivity drop by a factor 10, but no significant effect on the resistivity of the samples could be ascertained by variation of the drying conditions when samples had been subjected to subsequent annealing.

materials science, textiles
Study on Silk Fibroin Coated PET Fabric

DU Meng-Fang,MIN Si-jia,ZHANG Hai-Ping,FENG Qiang,ZHU Liang-Jun

DOI: https://doi.org/10.3969/j.issn.0257-4799.2007.03.016

2007-01-01

Abstract:Silk fibroin coated PET fabric was gained by coating silk fibroin onto chemical eroded PET fabric,and its physical-chemical properties and structure characters were studied.The results showed that weight-increasing rate of silk fibroin coated PET fabric arrived at 11.61%,the residual percentage after hot-water washing was 84.17%,and moisture regain rate was 3.8 times of non-coated PET fabric.After coating,breaking strength and breaking elongation of PET fabric were slightly reduced,but its electrostatic voltage peak and decay time were improved obviously.The infra-red spectrogram analysis showed that characteristic spectrogram of silk fibroin was detected in silk fibroin coated PET fabric.These results revealed that the property of silk fibroin coated PET fabric has been improved.
Development of a Screen-Printable Carbon Paste to Achieve Washable Conductive Textiles

Sheng Yong,Meijing Liu,Abiodun Komolafe,John Tudor,Kai Yang

DOI: https://doi.org/10.3390/textiles1030022

2021-10-05

Textiles

Abstract:Conductive tracks are key constituents of wearable electronics and e-textiles, as they form the interconnective links between wearable electrical devices/systems. They are made by coating or printing conductive patterns or tracks on textiles or by weaving, knitting, or embroidering conductive yarns into textiles. Screen printing is a mature and cost-effective fabrication method that is used in the textile industry. It allows a high degree of geometric freedom for the design of conductive patterns or tracks. Current screen-printed conductive textiles have the limitations of low durability when washed or when placed under bending, and they typically require encapsulation layers to protect the printed conductor. This paper presents a printable paste formulation and fabrication process based on screen printing for achieving a flexible and durable conductive polyester-cotton textile using an inexpensive carbon as the conductor. The process does not require an interface, the smoothing of the textile, or an encapsulation layer to protect the conductor on the textile. A resistivity of 4 × 10−2 Ω·m was achieved. The textile remains conductive after 20 standard washes, resulting in the conductor’s resistance increasing by 140%. The conductive textile demonstrated less than ±10% resistance variation after bending for 2000 cycles.
Surface Resistivity Of Pet/Cot Fabrics Treated With 3,4-Ethylenedioxythiophene Via Vapor Phase Polymerization

Qinguo Fan,Okan Ala,Jianzhong Shao,Jinqiang Liu

2010-01-01

Abstract:Flexible, permeable and electrically conducting textiles can be obtained via vapor phase polymerization (VPP) of 3,4-ethylenedioxythiophene (EDOT). By VPP, the polymerization reaction proceeds in the gas phase via/direct oxidation using an ionic dopant. In this VPP process, PEDOT was formed on PET/COT blend fabrics. The resultant surface resistivity on the PEDOT coated fabric materials achieved under optimized conditions is about 50-75 ohm/square, very close to that of ITO, while the textile materials remain soft, flexible, and permeable. This process did not use rigid inorganic conducting materials like ITO or a second polymeric component polystyrene sulfonic acid (PSS).
Fabrication of durable and conductive cotton fabric using silver nanoparticles and PEDOT:PSS through mist polymerization

Peng Wang,Yong Wang,Qingbo Xu,Qian Chen,YanYan Zhang,Zhenzhen Xu

DOI: https://doi.org/10.1016/j.apsusc.2022.153314

IF: 6.7

2022-08-01

Applied Surface Science

Abstract:Conductive cotton fabrics are widely used in electromagnetic shields and soft sensors because of their excellent softness and comfort. Generally, conductive cotton fabrics are prepared by depositing an inorganic conductive coating or an organic conductive polymer coating on them. However, due to the complex structure of cotton fabrics, these conductive coatings easily fall off and fracture under external forces, resulting in a sharp decline in the conductive properties of the finished fabrics. In the present work, L-cysteine was used as a binder to immobilize Ag NPs on cotton fabric. Ag NPs were covered by PEDOT:PSS to prevent them from falling off and cracking. As a result, the surface resistance of finished fabric was arrived at 8.7 Ω/sq. The finished fabric also exhibited excellent electromagnetic shielding effectiveness, with an electromagnetic shielding reached at 27.1 dB. Moreover, the composite coating significantly improved the durability of electrical conductivity and electromagnetic shielding properties of the finished fabric. In addition, mist polymerization was used to retain the inherent properties of the cotton fabric. We believe that the proposed method provides a new direction for the preparation of conductive cotton fabrics with a high stability.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Thermal electric effects and heat generation in polypyrrole coated PET fabrics

J. Avloni,L. Florio,A.R. Henn,A. Sparavigna

DOI: https://doi.org/10.4236/msa.2010.14037

2007-06-26

Abstract:Polypyrrole chemically synthesized on PET gives rise to textiles with a high electric conductivity, suitable for several applications from antistatics to electromagnetic interference shielding devices. Here, we discuss investigations on thermal electric performances of the polypyrrole coated PET in a wide range of temperatures above room temperature. The Seebeck coefficient turns out to be comparable with that of metal thermocouple materials. Since polypyrrole shows extremely low thermal diffusivities regardless of the electrical conductivity, the low thermal conductivity gives significant advantage to the thermoelectric figure-of-merit ZT, comparable with that of some traditional inorganic thermoelectric materials. The heat generation is also investigated for possible heating textile devices.

Materials Science
Reel-to-Reel Coating of a Conductive Polymer on Synthetic Textile Yarns in a Semi-closed Batch Oxidative CVD System

DOI: https://doi.org/10.1007/s12221-024-00596-3

IF: 2.5

2024-06-08

Fibers and Polymers

Abstract:In this manuscript, we demonstrate the ability to use a reel-to-reel processing technology for conductive surface functionalization of textile yarns using oxidative chemical vapor deposition in a continuous manner. We designed and built a vacuum deposition system, which allows the winding of yarns into the oCVD reactor by unreeling from the outside atmosphere, where the yarn is pre-treated with oxidant solution. Iron(III)chloride (FeCl 3 ) and 3,4-ethylenedioxythiophene were used as the oxidant and monomer, respectively, to deposit thin films of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films on the synthetic PET yarn surfaces. FTIR and XPS analyses were carried out to verify the chemical structure of as-deposited PEDOT films. Effects of temperature, oxidant concentration, and winding speed on the electrical conductivities of the yarns after oCVD were studied. All yarns exhibited non-zero conductivity values independent of the deposition conditions studied. Very high conductivity uniformities were observed along the longitudinal direction of the yarns even at the highest studied winding speed of 24 cm/min.

materials science, textiles,polymer science
A Solution Processable Flexible Transparent Conductive Graphene/PEDOT: PSS Film Fabricated by Spin and Blade Coating

Xiaozhu Fang,Zhijun Fan,Yichen Gu,Jiawen Shi,Min Chen,Xuewen Chen,Shaohua Qiu,Fatemeh Zabihi,Morteza Eslamian,Qianli Chen

DOI: https://doi.org/10.1007/s12204-018-1915-z

2018-01-01

Journal of Shanghai Jiaotong University (Science)

Abstract:Flexible transparent conductive films were made on PET substrates by spin and blade coating, using graphene sheets dispersed in PEDOT: PSS solution. Ultrasonic substrate vibration was used to improve microstructure and properties of the films. Comparing to the pristine PEDOT: PSS film, the sheet resistance is 3 to 4 orders of magnitude lower with the addition of graphene. The conductivity and reproducibility of the film are improved for two-layer films comparing to one-layer films, with a reduction in transparency. Films prepared with substrate vibration showed lower sheet resistance for one-layer films, as the size of dewetting areas is reduced. In addition, large-area flexible films with desirable conductivity and transmittance were successfully fabricated by blade coating, which is promising, as the process is low-cost, scalable and compatible with roll-to-roll manufacturing.
Smart flame retardant coating containing carboxymethyl chitosan nanoparticles decorated graphene for obtaining multifunctional textiles

Emad S. Goda,Mahmoud H. Abu Elella,Sang Eun Hong,Bidhan Pandit,Kuk Ro Yoon,Heba Gamal

DOI: https://doi.org/10.1007/s10570-021-03833-7

IF: 6.123

2021-03-30

Cellulose

Abstract:A revolutionary and straightforward technique with a dual functionality was manipulated for preparing graphene sheets (O-GRP) decorated with O-carboxymethyl chitosan nanoparticles (CMChNPs). Graphene was successfully exfoliated and decorated with CMChNPs through a simple ultrasonication tool. The developed graphene sheets were then utilized as the green binder for coating the surface of textile with the Ppy-Ag nanocomposite. A new vapor polymerization was used to synthesize the nanocomposite of polypyrrole-Ag on the graphene-modified fabric for acquiring ternary modified textiles (CT/O-GRP-Ppy-Ag). The structure and surface morphology of CMCh, O-GRP, and the various coated textiles have been carefully approved using various spectroscopic and microscopic analysis. The thermal stability, mechanical properties besides their electrical resistance, antimicrobial, and flame retardancy behaviors for the coated fabrics were investigated. The as-fabricated textile composites attained an inferior electrical resistance as 0.05 kΩ than that for the virgin textile (2770 kΩ) as an indication for the high conductive fabrics. The inhibition diameter zone for modified textiles was recorded as 24, and 28 mm for the E.coli, and S. aureus bacterial strains, respectively. Moreover, the rate of burning and LOI values for CT/O-GRP200-Ppy-Ag were significantly improved to 30.9 mm/min, and 22.8%, respectively compared to uncoated textile (149.3 mm/min, 17.8%), and the blank CT/O-GRP200 (79.2 mm/min, 19.9%) confirming the enhanced retardation against the fire growth.

materials science, textiles,polymer science, paper & wood
Characterisation of Electrical and Stiffness Properties of Conductive Textile Coatings with Metal Flake-Shaped Fillers

Veronica Malm,Fernando Seoane,Vincent Nierstrasz

DOI: https://doi.org/10.3390/ma12213537

IF: 3.4

2019-10-29

Materials

Abstract:Two conductive formulations containing different types of micron-sized metal flakes (silver-coated copper (Cu) and pure silver (Ag)) were characterised and used to form highly electrically conductive coatings (conductors) on plain and base-coated woven fabrics, the latter in an encapsulated construction. With e-textiles as the intended application, the fabric stiffness, in terms of flexural stiffness and sheet resistance (Rsh), after durability testing (laundering and abrasion) was investigated and related to user friendliness and long-term performance. Bare and encapsulated conductors with increasing amounts of deposited solids were fabricated by adjusting the knife coating parameters, such as the coating gap height (5, 20, 50, and 200 μm), which reduced the Rsh, as determined by four-point probe (4PP) measurements; however, this improvement was at the expense of increased flexural stiffness of the coated fabrics. The addition of a melamine derivative (MF) as a cross-linker to the Cu formulation and the encapsulation of both conductor types gave the best trade-off between durability and Rsh, as confirmed by 4PP measurements. However, the infrared camera images revealed the formation of hotspots within the bare conductor matrix, although low resistances (determined by 4PP) and no microstructural defects (determined by SEM) were detected. These results stress the importance of thorough investigation to assure the design of reliable conductors applied on textiles requiring this type of maintenance.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
A Green Electrically Conductive Textile with Tunable Piezoresistivity and Transiency

Pietro Cataldi,Pietro Steiner,Mufeng Liu,Gergo Pinter,Athanassia Athanassiou,Coskun Kocabas,Ian A. Kinloch,Mark A. Bissett

DOI: https://doi.org/10.1002/adfm.202301542

IF: 19

2023-04-27

Advanced Functional Materials

Abstract:Wearable electronics need green textile‐based conductors with tunable piezoresistivity and transiency. Such conductors are obtained by functionalizing cotton with green conductive inks. The modulation of the piezoresistivity and transiency is obtained by controlling the nanofiller geometry, binder composition, and textile twill orientation. This versatile green conductor may serve opposing needs by simply adjusting the material composition and the deformation direction. A green textile‐based conductor with controllable electrical resistance change with deformation and transiency (i.e., dissolution in water) will be the holy grail in wearable electronics since it can satisfy divergent needs with a single solution and be sustainable simultaneously. Nevertheless, designing such material is challenging since opposite requirements shall be satisfied. To solve such a problem, cotton is functionalized using conductive inks made of graphene or carbon nanofiber, a biodegradable polyvinyl alcohol binder, and environmentally friendly solvents. The electrical resistance shows an anisotropic response to bending depending on the composition of the coating and the stress direction, functioning either as a deformable compliant electrode or a tunable piezoresistor. Indeed, it can withstand thousands of bending cycles with a change in resistance of less than 5% or change its resistance by many orders of magnitude with the same deformation thanks to the combination of cotton twill and different nanofillers. A simple modification in the binder composition adding waterborne polyurethane allows the coating to go from entirely transient in water within minutes to withstanding simulated washing cycles for hours without losing its electrical conductivity. This green versatile conductor may serve opposing needs by altering the material composition and the deformation direction.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
Integrating high electrical conductivity and photocatalytic activity in cotton fabric by cationizing for enriched coating of negatively charged graphene oxide

Iftikhar Ali Sahito,Kyung Chul Sun,Alvira Ayoub Arbab,Muhammad Bilal Qadir,Sung Hoon Jeong

DOI: https://doi.org/10.1016/j.carbpol.2015.05.010

IF: 10.723

2015-10-01

Carbohydrate Polymers

Abstract:Electroconductive textiles have attended tremendous focus recently and researchers are making efforts to increase conductivity of e-textiles, in order to increase the use of such flexible and low cost textile materials. In this study, surface conductivity and photo catalytic activity of standard cotton fabric (SCF) was enhanced by modifying its surface charge, from negative to positive, using Bovine Serum Albumin (BSA) as a cationic agent, to convert it into cationised cotton fabric (CCF). Then, both types of fabrics were dip coated with a simple dip and dry technique for the adsorption of negatively charged graphene oxide (GO) sheets onto its surface. This resulted in 67.74% higher loading amount of GO on the CCF making self-assembly. Finally, this coating was chemically converted by vapor reduction using hydrazine hydrate to reduced graphene oxide (rGO) for restoration of a high electrical conductivity at the fabric surface. Our results revealed that with such high loading of GO, the surface resistance of CCF was only 40Ω/sq as compared to 510Ω/sq of the SCF and a 66% higher photo catalytic activity was also achieved through cationization for improved GO coating. Graphene coated SCF and CCF were characterized using FE-SEM, FTIR, Raman, UV-vis, WAXD, EDX and XPS spectroscopy to ascertain successful reduction of GO to rGO. The effect of BSA treatment on adsorption of cotton fabric was studied using drop shape analyzer to measure contact angle and for thermal and mechanical resistance, the fabric was tested for TGA and tensile strength, respectively. rGO coated fabric also showed slightly improved thermal stability yet a minor loss of strength was observed. The high flexibility, photocatalytic activity and excellent conductivity of this fabric suggests that it can be used as an electrode material for various applications.

polymer science,chemistry, organic, applied

Conductive textiles prepared by spray coating of water-based graphene dispersions

Effects of three fabric weave textures on the electrochemical and electrical properties of reduced graphene/textile flexible electrodes

PET/Graphene Nanocomposite Fibers Obtained by Dry-Jet Wet-Spinning for Conductive Textiles

Developing Graphene‐based Conductive Textiles Using Different Coating Methods

Preparation and characterization of high-performance water-based graphene dispersions for conductive coating on textiles

The Influence of Substrate Functionalization for Enhancing the Interfacial Bonding between Graphene Oxide and Nonwoven Polyester

Elaboration of a Conductive Textile by Coating for Clothes Equipped with Fourth-Generation Photovoltaic Cells

Surface Characterization and Electrical Properties of Spin- Coated Graphene Conductive Film

A Facile Approach of Fabricating Electrically Conductive Knitted Fabrics Using Graphene Oxide and Textile-Based Waste Material

Electrically conductive textile coating with a PEDOT-PSS dispersion and a polyurethane binder

Study on Silk Fibroin Coated PET Fabric

Development of a Screen-Printable Carbon Paste to Achieve Washable Conductive Textiles

Surface Resistivity Of Pet/Cot Fabrics Treated With 3,4-Ethylenedioxythiophene Via Vapor Phase Polymerization

Fabrication of durable and conductive cotton fabric using silver nanoparticles and PEDOT:PSS through mist polymerization

Thermal electric effects and heat generation in polypyrrole coated PET fabrics

Reel-to-Reel Coating of a Conductive Polymer on Synthetic Textile Yarns in a Semi-closed Batch Oxidative CVD System

A Solution Processable Flexible Transparent Conductive Graphene/PEDOT: PSS Film Fabricated by Spin and Blade Coating

Smart flame retardant coating containing carboxymethyl chitosan nanoparticles decorated graphene for obtaining multifunctional textiles

Characterisation of Electrical and Stiffness Properties of Conductive Textile Coatings with Metal Flake-Shaped Fillers

A Green Electrically Conductive Textile with Tunable Piezoresistivity and Transiency

Integrating high electrical conductivity and photocatalytic activity in cotton fabric by cationizing for enriched coating of negatively charged graphene oxide