Preparation of hyper-crosslinked polymer derived porous carbon and its electrochemical properties
Xiaoyi Chen,Xinguo Chen,Leyao Li,Xia Zhao,Jianqiang Zhang,Shenglong Hu,Heming Luo
DOI: https://doi.org/10.1007/s10854-023-11478-4
2023-10-22
Journal of Materials Science Materials in Electronics
Abstract:Hyper-crosslinked polymers, with dense crosslinking, are a class of organic materials, preventing the close stacking of polymer chains. They are one of the representative carbon precursors. With the solvothermal method, hyper-crosslinked polymers were prepared in this paper. By using the hyper-crosslinked polymers as carbon precursors, a porous carbon (PC) material was derived from hyper-crosslinked polymers (PNOC-T-y) with high temperature charring-chemical activation, thereby exploring the influence of carbonization temperature (CT) and KOH activator ratio on microstructure and electrochemical properties (ECP) of the derived PC. As exhibited by the results, the derived PC PNOC-800-3 has a three-dimensional porous structure with abundant internal microporous and mesoporous structure, possessing specific surface area (S BET ) of 3094.51 m 2 g −1 , and the mean pore size is 1.89 nm. Due to more active sites provided by this structure for charge and electrolyte ion adsorption, the adsorption and aggregation capacity of charge and electrolyte ions are effectively improved. At the current density (CD) of 1 A g −1 , the specific capacitance (SC) of the derived PC PNOC-800-3 was 247.3 F g −1 . During the increase of CD from 1 to 10 A g −1 , the decay rate was 20.68%. When CD was 1 A g −1 , the capacitance retention rate was 87.79% after 5000 cycles, and the Coulomb efficiency was 100% around. When CD maintains at 1 A g −1 , the energy density (ED) was 8.47 Wh kg −1 at the power density (PD) of 500 W kg −1 , indicating its favorable electrochemical performance.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied