Abstract:The effect of cooling on the brittleness of glasses in general, and bulk metallic glasses (BMGs) in particular, is usually studied with continuously varying cooling rates; slower cooling rates lead to stiffer, harder, and more brittle glasses than higher cooling rates. These protocols obscure any potential discontinuity that a glass might experience depending on whether its microstructure resembles that of a fragile or a strong glass-forming liquid. Here, we use large-scale molecular dynamics to simulate the nanoindentation behavior of model BMGs (Zr$_{0.6}$Cu$_{0.3}$Al$_{0.1}$) obtained by rapidly quenching equilibrium melts from temperatures above and below the fragile-to-strong transition temperature $T_\textrm{fst}$, leading to fragile and strong glasses, respectively. While the contact modulus deduced from the indentation simulation evolves smoothly with the temperature $T_\text{q}$ from which the melt is quenched, the plastic response changes quasi-discontinuously as $T_\text{q}$ passes through $T_\textrm{fst}$. In particular, strong glasses develop highly asymmetric flow profiles with mature shear bands, in contrast to fragile glasses. Quantitative differences reveal themselves not only through a formal von Mises localization parameter analysis but also through image analysis of flow patterns using pre-trained artificial intelligence models. Moreover, seemingly erratic flow profiles for our indentation geometry produced surprisingly reproducible and, thus, deterministic features. It remains to be determined to what extent other classes of glass formers follow our observation that the degree of brittleness is significantly influenced by whether the melt is fragile or strong when it falls out of equilibrium at the glass transition temperature.

Observation of an apparent first-order glass transition in ultrafragile Pt–Cu–P bulk metallic glasses

Size-Dependent Brittle-To-Ductile Transition in Silica Glass Nanofibers

Formation of two glass phases in binary Cu-Ag liquid

Reentrant glass transition leading to ultrastable metallic glass

Anomalous Crystallization As A Signature of the Fragile-To-Strong Transition in Metallic Glass-Forming Liquids

Observation of an isothermal glass transition in metallic glasses

Mechanical glass transition revealed by the fracture toughness of metallic glasses

On the glass transition in metallic melts

Activation energy spectrum for relaxation and polyamorphism in an ultra-viscous metallic glass former

Structural Behavior of Pd40Cu30Ni10P20 Bulk Metallic Glass below and above the Glass Transition

Evidence for a simple monatomic ideal glass former: the thermodynamic glass transition from a stable liquid phase

Solid-solid phase transition via the liquid in a Pd43Cu27Ni10P20 bulk metallic glass under conventional conditions

Glass Transitions and Critical Points in Orientationally Disordered Crystals and Structural Glassformers: "Strong" Liquids are More Interesting Than We Thought

First-order transitions in glasses and melts induced by solid superclusters nucleated and melted by homogeneous nucleation instead of surface melting

Brittleness of metallic glasses dictated by their state at the fragile-to-strong transition temperature

In situ scattering study of multiscale structural evolution during liquid–liquid phase transition in Mg-based metallic glasses

First-Order Phase Transition in Liquid Ag to the Heterogeneous G-Phase

Critical behavior of the fluctuation heat capacity near the glass transition of metallic glasses

Non-equilibrium first order transition marks the mechanical failure of glasses

Structural Evolution During Fragile-to-strong Transition in CuZr(Al) Glass-Forming Liquids.

Manifestation of Dynamic Anomaly in Metallic Glass-Forming Liquids by Their Crystallization Processes