Abstract:Urea–formaldehyde (UF) and phenol–formaldehyde (PF) resins are the most widely used adhesives in the production of wood composites, and are cured through hot-pressing to provide adhesion strength with the composites. This study investigates the relationship between thermal curing behavior monitored by differential scanning calorimetry (DSC) and adhesive bond strength development measured by an automated bonding evaluation system (ABES) for UF and PF resins with different molecular weights ( M w ). DSC results demonstrated that UF resins cured faster than PF resins, as indicated by a lower apparent activation energy ( E a ). In addition, UF and PF resins with lower M w cured faster in the early stages of curing and slower in the latter stages of curing as compared to higher- M w resins. Furthermore, according to the ABES results, when increasing the molecular weight, both UF and PF resins exhibited greater adhesive bond strength, irrespective of pressing parameters (temperature and time). The isothermal DSC and ABES results demonstrated that the adhesive bond strength increased with an increase in the degree of cure of the resins, indicating a correlation between them. It also showed that UF resins attained optimal adhesive bond strength at low temperature (110–130 °C) in roughly 180 s while PF resins attained it at high temperature (120–130 °C) in about 300 s. However, the degree of cure under isothermal scans was inconsistent with temperatures. These results indicate that the degree of cure is closely related to the adhesion strength development of UF and PF resins which are curing at low and high temperatures to obtain the optimum adhesion strength.

Determination of Crystallinity of Thermosetting Urea-Formaldehyde Resins Using Deconvolution Method

Determination of formaldehyde/urea molar ratio in amino resins by near-infrared spectroscopy

Studies on unstable structures in urea-formaldehyde resins prepared in strong acid medium

Study on the Evolvement of Structure in Synthesis of Urea-Formaldehyde Resins by Ftir

Study on structure and properties of glyoxal-urea-formaldehyde copolycondensation resin

Relationship between thermal curing behavior and bond strength development in formaldehyde-based resins with different molecular weights

Thermal Behavior Analysis of Melamine Modified Urea-Formaldehyde Resin with Different Molar Ratios

H2O2 catalytic cure of urea formaldehyde resins with different structures

Thermal degradation and curing kinetic study of urea formaldehyde/l-tyrosine composites

Low Mole Ratio UF and UMF Resins Entailing Uron-Type Methylene-Ether Groups and their Low Formaldehyde Emission Potentials

The hydrolytic stability and structure of the cured melamine-urea-formaldehyde resin

Prediction of Residual Curing Capacity of Melamine-Formaldehyde Resins at an Early Stage of Synthesis by In-Line FTIR Spectroscopy

The impact of altering the molar ratio on formaldehyde content and the physical and mechanical properties of MDF panels

An Empirical Method for Estimating the Degree of Crystallinity of Native Cellulose Using the X-Ray Diffractometer

In Situ FT‐IR‐ATR Studies on the Structure Development of Polyurethane‐urea Systems

Characterization of urea–formaldehyde resin penetration into medium density fiberboard fibers

Crystallization of PVDF in the PVDF/PMMA blends precipitated from their non-solvents: special “orientation” behavior, morphology, and thermal properties

In situ FTIR study on melting and crystallization of polyhydroxyalkanoates

Effect of a crystalline resin on the curing behavior of unsaturated polyester resin systems

Correlation of Mechanical and Chemical Cure Development for Phenol–formaldehyde Resin Bonded Wood Joints

In-situ modification of low molar ratio urea–formaldehyde resins with cellulose nanofibrils for plywood