Highly Efficient and Robust MoS 2 Nanoflake-Modified-TiN-Ceramic-Membrane Electrode for Electrocatalytic Hydrogen Evolution Reaction
Kai Lv,Dewen Zheng,Yangyang Shi,Xi Zhang,Feihong Wang,Jianming Li,Shanyu Wang,Binbin Dong,Lu Yuan Hao,Liangjun Yin,Xin Xu,Yuxi Xian,Simeon Agathopoulos
DOI: https://doi.org/10.1021/acsaem.1c00784
IF: 6.4
2021-07-14
ACS Applied Energy Materials
Abstract:Electrode design and fabrication are of major importance for hydrogen evolution reaction applications, as far as high-efficiency and low-cost production of hydrogen are concerned. This paper reports on a titanium-nitride-ceramic-membrane electrode modified by MoS<sub>2</sub> nanoflakes. Porous TiN-ceramic membranes were fabricated by phase-inversion tape-casting, followed by pressureless sintering. The as-prepared TiN membranes contained straight finger-like pores with an average diameter of 80 μm and smaller pores with an average diameter of 1–3 μm. Then, MoS<sub>2</sub> nanoflakes were perpendicularly, densely, and uniformly grown on the surface of the TiN grains through the one-pot hydrothermal method. The optimized MoS<sub>2</sub>/TiN membrane electrode displayed a low overpotential of 113 mV at 10 mA cm<sup>–2</sup>, a Tafel slope of 78 mV dec<sup>–1</sup>, a small charge transfer resistance of 1.44 Ω, and a high double-layer capacitance of 504 mF cm<sup>–2</sup>. It also exhibited excellent stability with slight degradation after 80 h testing at an overpotential of 150 mV in 0.5 M H<sub>2</sub>SO<sub>4</sub>. The high conductivity of the TiN substrate, the similar chemical bonds, which favored the rapid electron transfer between MoS<sub>2</sub> and TiN, the abundant exposed active sites of MoS<sub>2</sub> nanoflakes, and the unique dual-pore structure resulted in the above superior electrocatalytic activity. The proposed successful utilization of conventional ceramic-membrane technology to prepare electrocatalysts based on membrane electrodes has potential for large-scale application in industrial hydrogen production.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00784?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00784</a>.Photographs of TiN green tapes and experimental device, SEM images of the finger-like layer and MoS<sub>2</sub>/TiN with various amounts of Mo and S precursors at the same ratio of Mo and S (1:4), XPS spectra of MoS<sub>2</sub>/TiN-1:2 and MoS<sub>2</sub>/TiN-1:8, cyclic voltammogram curves of pristine TiN, MoS<sub>2</sub>/TiN-1:2, MoS<sub>2</sub>/TiN-1:4, and MoS<sub>2</sub>/TiN-1:8, polarization curves of MoS<sub>2</sub>/TiN with various amounts of Mo and S precursors at the same ratio of Mo and S (1:4), comparison of electrocatalysts, and EIS data (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00784/suppl_file/ae1c00784_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels