Abstract:This study provides an analysis of the phosphorus adsorption efficacy of three modified drinking water treatment residues (MDWTRs): MDWTR-P (powdered form), MDWTR-D2, and MDWTR-D5 (alginate bead-entrapped forms with bead diameters of 2 mm and 5 mm, respectively). The preparation process involved washing and drying the drinking water treatment residue, followed by grinding and sieving to achieve particle sizes below 90 μm. The residue was then incinerated at 600 °C in oxygen-limited conditions. Subsequently, the MDWTR was formulated into alginate beads by mixing with sodium alginate and FeCl3 solutions, resulting in spherical particles of specified diameters. The evaluation of surface area, pore volume, pore size, and CHN concentration revealed that MDWTR-D5 possesses the largest surface area (284.7 m2 g-1) and highest micropore volume (0.04 cm3 g-1), indicating a greater capacity for adsorption. SEM-EDS analysis demonstrated significant compositional changes post-treatment, particularly elevated phosphorus levels, confirming effective adsorption. Metal content analysis indicated high aluminum levels in MDWTR-P and increased iron content in MDWTR-D5. Toxicity Characteristic Leaching Procedure (TCLP) and in vitro bioaccessibility (IVBA) tests confirmed the non-hazardous nature of all MDWTRs, ensuring their safety for environmental applications. Kinetic analyses using pseudo-first-order, pseudo-second-order, and intraparticle diffusion models highlighted the superior performance of MDWTR-D5, with the highest equilibrium adsorption capacity and initial adsorption rate across all tested concentrations, suggesting both high efficiency and rapid adsorption potential. Further validation using Langmuir and Freundlich isotherms revealed MDWTR-D5's highest monolayer adsorption capacity (22.88 mg g-1) and Freundlich adsorption capacity parameter (6.97 mg g-1). Statistical analysis via one-way ANOVA confirmed significant differences in phosphorus concentrations among the MDWTRs samples (p-value <0.001), consistently underscoring MDWTR-D5's superior adsorption performance. These findings highlight MDWTR-D5's potential as an effective adsorbent for phosphorus removal in wastewater treatment, emphasizing its applicability in environmental remediation strategies.

Utilization of alum sludge as adsorbent for phosphorus removal in municipal wastewater: A review

Use of wastewater alum-coagulation sludge as a phosphorus fertiliser – a mini review

Two strategies for phosphorus removal from reject water of municipal wastewater treatment plant using alum sludge

Effect of Adding Alum Sludge from Water Treatment Plant on Sewage Sludge Dewatering

Phosphorus Adsorption Characteristics of Alum Sludge: Adsorption Capacity and the Forms of Phosphorus Retained in Alum Sludge

Sequential wet extraction of phosphorus from sewage sludge using alum sludge: Reassessing the aluminium-phosphorus speciation using experimental and simulation approach

Effectiveness of a drinking-water treatment sludge in removing different phosphorus species from aqueous solution

Phosphate adsorption on dried alum sludge: Modeling and application to treatment of dairy effluents

Enhanced phosphate adsorption studies on several metal-modified aluminum sludge: preparation optimization, adsorption behavior, and mechanistic insight

Key issues to consider when using alum sludge as substrate in constructed wetland

Recycling of sludge residue as a coagulant for phosphorus removal from aqueous solutions

A comprehensive investigation to the fate of phosphorus in full-scale wastewater treatment plants using aluminum salts for enhanced phosphorus removal

Remove and Recover Phosphorus During Anaerobic Digestion of Excess Sludge by Adding Waste Iron Scrap

The use of alum sludge to improve cereal production on a nutrient-deficient soil

Tuning adsorption capacity of metal–organic frameworks with Al3+ for phosphorus removal: Kinetics, isotherm and regeneration

Phosphorus removal from wastewaters: Experimental and theoretical support for alternative mechanisms

Recent advances in the removal and recovery of phosphorus from aqueous solution by metal-based adsorbents: A review

Enhanced phosphorus adsorption using modified drinking water treatment residues: A comparative analysis of powder and alginate bead forms

Nutrient removal in floating and vertical flow constructed wetlands using aluminium dross: An innovative approach to mitigate eutrophication

Application of Alum Sludge in Wastewater Treatment Processes: “Science” of Reuse and Reclamation Pathways

Trends in the recovery of phosphorus in bioavailable forms from wastewater