Abstract:Cu-based catalysts are widely employed for CO or CO2 hydrogenation into methanol. However, their catalytic performance highly depends on supports, and the real evolution of Cu species is still covered by active components. Herein, we supply a Cu/SiO2 catalyst prepared by flame spray pyrolysis (FSP), showing catalytic performance comparable to that of the active Cu/ZrO2 catalyst for methanol synthesis from CO2. It reaches 79% selectivity at a CO2 conversion of 5.2%, which is an outstanding selectivity among previously reported Cu/SiO2 catalysts, considering they are generally treated as nearly inert catalysts. In situ X-ray absorption spectroscopy (XAS) analysis shows that 5 times more Cu+ species in the FSP-Cu/SiO2 are stabilized in comparison to those in the traditional ammonia evaporation (AE) made catalyst even after reduction at 350 °C. A unique shattuckite-like precursor with a slightly distorted Cu–O–Si texture structure formed in the FSP-made catalyst is responsible for the enriched Cu+ species. Variations of intermediate formation and methanol production are found to have a good relationship with the amount of Cu+ species. According to the results of high-pressure in situ DRIFTS, we attribute this to the promotional effect of Cu+ on the stabilization of CO* intermediates, which inhibits CO desorption and facilitates further hydrogenation to CH3OH via the RWGS + CO-Hydro pathway. These results bring insights into the Cu reduction behavior and the function of Cu+ species during methanol production on Cu-based catalysts without the assistance of active supports.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c04371?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c04371</a>.Catalytic performances, FTIR, TEM, XRD, XAS, CO-IR, CO-TPD, in situ DRIFTS and catalyst structure (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c04371/suppl_file/cs0c04371_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Silica accelerates the selective hydrogenation of CO2 to methanol on cobalt catalysts

Silica-modulated Cu-ZnO-Al2O3 catalyst for efficient hydrogenation of CO2 to methanol

Unraveling the tunable selectivity on cobalt oxide and metallic cobalt sites for CO 2 hydrogenation

Stable Cu δ+ species - Catalyzed CO2 hydrogenation to methanol in silanol nests on Cu/S-1 catalyst

Product Selectivity Controlled by Nanoporous Environments in Zeolite Crystals Enveloping Rhodium Nanoparticle Catalysts for CO2 Hydrogenation

Molecular-Level Insight into How Hydroxyl Groups Boost Catalytic Activity in CO2 Hydrogenation into Methanol

Core–shell structured Cu@m-SiO2 and Cu/ZnO@m-SiO2 catalysts for methanol synthesis from CO2 hydrogenation

Mesoporous Manganese-Cobalt Oxide Spinel Catalysts for CO2 Hydrogenation to Methanol

Core–shell silica@Cu x ZnAl LDH catalysts for efficient CO 2 hydrogenation to methanol

Selective Hydrogenation of CO2 to Ethanol over Cobalt Catalysts

Spinel Nanostructures for the Hydrogenation of CO2 to Methanol and Hydrocarbon Chemicals

Isolated dual-active Fe-Co sites efficiently promote CO 2 hydrogenation upgrading

Cobaltous Oxide Supported on MFI Zeolite As an Efficient Ethane Dehydrogenation Catalyst

COx hydrogenation to methanol and other hydrocarbons under mild conditions with Mo3S4@ZSM-5

Efficient production of methanol and diols via the hydrogenation of cyclic carbonates using copper–silica nanocomposite catalysts

Co-Based Catalysts Supported on Silica and Carbon Materials: Effect of Support Property on Cobalt Species and Fischer–Tropsch Synthesis Performance

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol

Combining Atomic Layer Deposition with Surface Organometallic Chemistry to Enhance Atomic-Scale Interactions and Improve the Activity and Selectivity of Cu-Zn/SiO2 Catalysts for the Hydrogenation of CO2 to Methanol

Theoretical Insights into Amido Group-Mediated Enhancement of CO2 Hydrogenation to Methanol on Cobalt Catalysts.

Stabilizing Cu + in Cu/SiO 2 Catalysts with a Shattuckite-Like Structure Boosts CO 2 Hydrogenation into Methanol

A highly efficient Li-Cu/MoO x catalyst constructed by a precursor dispersion and alkali metal promotion stepwise regulation strategy for CO 2 hydrogenation to methanol reaction