Abstract:This paper conducts compressive strength tests on foam concrete prepared under four factors and three levels through the design of orthogonal experiments. It delves into the phase change rules of the load–displacement curves obtained under various mix proportions. Furthermore, based on the 1-day and 3-day compressive strength values, the study explores different mix proportion results using range analysis and variance analysis methods, thereby determining the optimal mix proportion that can satisfy the maximum 1-day and 3-day compressive strength values. The results indicate that the compression process of rapid-hardening foam concrete includes four stages: initial compaction stage, elastic stage, yielding stage, and plateau stage, with each stage having different causes. Additionally, the sensitivity sequence of factors affecting the 1-day and 3-day compressive strength of rapid-hardening foam concrete is respectively rapid sulfoaluminate cement (α) > water-reducing agent content (δ) > foam content (β) > water-cement ratio (γ) and rapid sulfoaluminate cement (α) > water-cement ratio (γ) > foam content (β) > water-reducing agent content (δ). With 100% sulfoaluminate cement content, the 1-day and 3-day compressive strength values can reach 1.7054 and 2.5471 MPa, respectively, which are 13 times and 7 times the minimum values of 1-day and 3-day compressive strength under other admixtures. The analysis shows that the content of rapid sulfoaluminate cement has the most significant effect on the 1-day and 3-day compressive strength of rapid-hardening foam concrete, with foam content having the least impact on 1-day compressive strength and water-reducing agent content having the least impact on 3-day compressive strength. By integrating range analysis and variance analysis, the optimal mix proportion that simultaneously satisfies the maximum 1-day and 3-day compressive strength is determined to be 100% content of rapid-hardening sulfoaluminate cement, 4% foam content, 0.55% cement ratio, and 0.12% admixture content. Overall, this study provides theoretical support for the research and development of new rapid-hardening foam concrete materials and has significant practical implications for the emergency repair and construction of infrastructure projects.

Study on influencing factors of mechanical properties of ceramsite foam concrete based on orthogonal test

Study on the preparation and performances analysis of lightweight high strength ceramsite aerated concrete

Optimization of coal-based solid waste ceramsite foam concrete mix proportions and performance study

Optimization of Preparation of Foamed Concrete Based on Orthogonal Experiment and Range Analysis

Experimental Study on Performance Influencing Factors and Reasonable Mixture Ratio of Desert Sand Ceramsite Lightweight Aggregate Concrete

Study on the Performance of Foam Concrete Prepared from Decarburized Fly Ash

Mix proportion optimization and early strength development in modified foam concrete: an experimental study

Preparation and Properties of Foam Concrete Incorporating Fly Ash

Effect of Sand-to-Cement Ratio on Mechanical Properties of Foam Concrete

The Workability and Mechanical Performance of Fly Ash Cenosphere–Desert Sand Ceramsite Concrete: An Experimental Study and Analysis

Effect Analysis of Soil Type and Silt Content on Silt-Based Foamed Concrete with Different Density

Effects of Mixing Techniques and Material Compositions on the Compressive Strength and Thermal Conductivity of Ultra-Lightweight Foam Concrete

Effect of Water-Cement Ratio on Pore Structure and Strength of Foam Concrete

Influence of bottom ash and polypropylene fibers on the physico-mechanical, durability and thermal performance of foam concrete: An experimental investigation

Proportion and Performance Optimization of Lightweight Foamed Phosphogypsum Material Based on an Orthogonal Experiment

Investigating the Mechanical and Durability Characteristics of Fly Ash Foam Concrete

Preparation of foam ceramics from solid wastes: a study on the relationship between firing regime and properties by grey system theory

Optimal Mix Design and Mechanical Properties of Rapid-Hardening Foam Concrete

An Investigation of the Properties of Expanded Polystyrene Concrete with Fibers Based on an Orthogonal Experimental Design

Influencing factors of mechanical and thermal conductivity of foamed phosphogypsum-based composite cementitious materials

Experimental Investigation on the Influencing Factors of Compressive Strength of Foamed Lightweight Material Utilizing Completely Decomposed Granite