Abstract:With the extensive exploitation of ocean resources, the steels used in ocean engineering have been developed towards the trend of high strength-toughness and thick plates, which consequently causes welding problem and high risk of stress corrosion cracking (SCC). The heat-affected zone (HAZ) of high-strength low-alloy steel undergoes phase transformation during welding thermal cycle and it's generally considered to be most vulnerable to SCC. E690 steel, as a newly-developed high strength steel, is currently the leading kind of steel used in ocean platform for its excellent performance. However, there is few research about its SCC behavior in marine atmosphere, especially in SO2-polluted atmosphere. Therefore, it's of great importance to investigate the SCC behavior and mechanism of simulated HAZ of E690 steel in this environment. However, the HAZ is a narrow zone including various microstructures; thus, the individual performance of different microstructures is inconvenient to study. In this work, various microstructures in HAZ, including coarse grained heat-affected zone (CGHAZ), fine grained heat-affected zone (FGHAZ) and intercritical heat-affected zone (ICHAZ), were simulated by heat treatment according to real HAZ microstructures of E690 steel. A comparative study of SCC behaviors of various HAZ microstructures in simulated SO2-containing marine atmosphere was conducted by using U-bend specimen corrosion test under dry/wet cyclic condition. The results indicated that various HAZ microstructures have high susceptibility to SCC in this environment. The SCC susceptibility of CGHAZ and ICHAZ is very high with a high crack growth rate while that of FGHAZ and parent metal is relatively modest. SCC cracks were initiated after 5 d of cyclic corrosion test for U-bend specimen of various microstructures. The microcracks were initiated from the corrosion pits, which were induced by the galvanic corrosion between martensite-austenite (M-A) constituents and ferritic matrix.

Comparative study on corrosion fatigue behaviour of high strength low alloy steel and simulated HAZ microstructures in a simulated marine atmosphere

Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment

Comparative Study of the Scc Behavior of E690 Steel and Simulated Haz Microstructures in A So2-Polluted Marine Atmosphere

Corrosion fatigue cracking behaviors of Q690qE high‐strength bridge steel as a weld joint in simulated marine environment

Experimental Research on Fatigue Performance of Corroded Q690 High-Strength Steel

Influence of Different Heat-Affected Zone Microstructures on the Stress Corrosion Behavior and Mechanism of High-Strength Low-Alloy Steel in a Sulfurated Marine Atmosphere

Experimental Study on Fatigue Crack Growth and Residual Strength of Aluminium Alloy 2024-T3 under Mixed Corrosive Environments

Corrosion evolution and stress corrosion cracking behavior of a low carbon bainite steel in the marine environments: Effect of the marine zones

Experimental Research on Fatigue Performance of Butt Welds of Corroded Q690 High Strength Steel

Hydrogen Permeation and Stress Corrosion Cracking of Heat-Affected Zone of E690 Steel under the Combined Effect of Sulfur Species and Cathodic Protection in Artificial Seawater

Effect of micro-galvanic corrosion on corrosion fatigue cracking of the weld joint of high strength bridge steel

Influence of cementite coarsening on the corrosion resistance of high strength low alloy steel

Experimental and Numerical Investigation on Mechanical and Fatigue Performance of Corroded Q690D High-Strength Steel

Microstructural Evolution and Oxidation Behaviour of CF8A Austenitic Stainless Steel During Corrosion Fatigue in a Simulated Pressurised Water Reactor Environment

Effect of Cathodic Potential on Stress Corrosion Cracking Behavior of Different Heat-Affected Zone Microstructures of E690 Steel in Artificial Seawater

The Corrosion Fatigue of Medium Strength Structural Steels

Investigation on the Fatigue Crack Growth Behavior of Welded Joints in EH690 High-Strength Marine Steel

Mechanistic Understanding on the Fatigue Cracking in Fretting Corrosion of Alloy 690TT under Partial Slip Regime in 100 ℃ and 290 ℃ Water

Corrosion Fatigue Behaviour of Q690D High-Strength Steel Considering the Effect of Coupling

The Corrosion Characterization in Simulated Heat-Affected Zones of X80 Pipeline Steel in Near-Neutral Solution

Study on fatigue behavior of butt-welded high-strength steel connections with surface cracks