Abstract:In this work, using the methods of X-ray phase analysis, transmission electron microscopy, X-ray photoelectron spectroscopy and Raman spectroscopy, the features of the impact of annealing in air within the temperature range of t = 200÷÷550 °C on the morphology, elemental and phase composition, chemical state and structure of primary particles of nanopowders obtained by grinding natural diamond and the method of detonation synthesis are studied. It is shown that heat treatment in air at given values of temperature and heating time does not affect the elemental composition and atomic structure of primary particles of nanopowders obtained both by the methods of detonation synthesis (DND) and natural diamond grinding (PND). Using XPS, Raman spectroscopy, and transmission electron microscopy, it has been found that annealing in air within the temperature range of 400–550 °C results in the effective removal of amorphous and graphite-like carbon atoms in the sp2- and sp3-states from diamond nanopowders by oxidation with atmospheric oxygen. In the original DND nanopowder, containing about 33.2 % of non-diamond carbon atoms of the total number of carbon atoms, after annealing for 5 h at a temperature of 550 °C, the relative number of nondiamond carbon atoms in the sp2-state decreased to ~21.4 %. In this case, the increase in the relative number of carbon atoms in the sp3-state (in the lattice of the diamond core) and in the composition of oxygen-containing functional groups ranged from ~39.8 % to ~46.5 % and from ~27 % to ~32.1 %, respectively. In the PND nanopowder, which prior to annealing contains about 10.6 % of non-diamond carbon atoms in the sp2-state of the total number of carbon atoms, after annealing under the same conditions as the DND nanopowder, their relative number decreased to 7.1 %. The relative number of carbon atoms in the sp3-state increased from 72.9 % to 82.1 %, and the proportion of carbon atoms in the composition of oxygen-containing functional groups also slightly increased from 10.2 % to 10.8 %. It is demonstrated that the annealing of PND and DND nanopowders in air leads to a change in their color, they become lighter as a result of oxidation of non-diamond carbon by atmospheric oxygen. The maximum effect is observed at a temperature of 550 °C and an annealing time of 5 h. In this case, the weight loss of PND and DND nanopowders after annealing was 5.37 % and 21.09 %, respectively. The significant weight loss of DND nanopowder compared to PND is primarily caused by the high content of non-diamond carbon in the initial state and the high surface energy of primary particles due to their small size.

Morphology and Structural State of Particles of Nanopowders Prepared by Milling of Natural Diamond and by Detonation Synthesis

Extrastrong aggregates of detonation nanodiamonds: structure and formation

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Core–Shell Composites Based on Partially Oxidized Blend of Detonation Synthesis Nanodiamonds

The growth of agglomerates in the conditions of detonation synthesis of diamond

Fabrication process independent and robust aggregation of detonation nanodiamonds in aqueous media

Observation of Conducting Structures in Detonation Nanodiamond Powder by Electron Paramagnetic Resonance

Determination of Non-Combustible Impurities in Detonation Diamond Nanopowder

Study on the Polycrystalline Mechanism of Polycrystalline Diamond Synthesized from Graphite by Direct Detonation Method

Structure formation of ultradispersed diamond by detonation synthesis

Detonation Synthesis Nanodiamond Soot as a Promising Filler for Polymer Composites

A Theoretical Insight for Nucleation of Diamond-like Carbon

Air-thermal oxidation of diamond nanopowders obtained by the methods of mechanical grinding and detonation synthesis

[Studies on nano-diamond prepared by explosive detonation by Raman and infrared spectroscopy]

Study on Morphologies and Structures of Diamond Films Synthesized on Cemented Carbide Substrates

Surface Functionalization and Structure Characterizations of Nanodiamond and Its Epoxy Based Nanocomposites

Diamond–SiC nanocomposites sintered from a mixture of diamond and silicon nanopowders

Microstructural Study of Synthetic Sintered Diamond and Comparison with Carbonado, A Natural Polycrystalline Diamond

Scalable Reshaping of Diamond Particles via Programmable Nanosculpting

Synthesis and Mechanism Study of Carbon Nanowires, Carbon Nanotubes, and Carbon Pompons on Single-Crystal Diamonds

Synthesis of twin-structured nanodiamond particles