Effect of ultrasonic impact treatment on surface stress evaluation of laser cladding coating by using critically refracted longitudinal wave
Bin Liu,Yingming Yu,Ruifeng Li,Jiayang Gu,Peng He
DOI: https://doi.org/10.1016/j.surfcoat.2021.127484
IF: 4.865
2021-09-01
Surface and Coatings Technology
Abstract:<p>Based on the <em>L</em><sub>cr</sub> wave acoustoelastic effect, surface stress of laser cladding Fe314 alloy coating after ultrasonic impact treat (UIT) was measured, and relation between <em>L</em><sub>cr</sub> wave acoustoelastic coefficient and repetition rate of UIT was discussed in this paper. The laser cladding Fe314 alloy coating was prepared on surface of carbon steel and impacted with different repetition rates of UIT by using UIT-300 system. After that, the experimental system of stress measurement with <em>L</em><sub>cr</sub> wave, consisting of a ultrasonic wave generator, a digital oscilloscope and two <em>L</em><sub>cr</sub> wave transducers (including one transmitting transducer and one receiving transducer) with 2.5MHz frequency, was used to collect <em>L</em><sub>cr</sub> waves of coating with calibration test, and then the difference in time of flight between <em>L</em><sub>cr</sub> waves was calculated with the cross correlation theory. To explain experimental results, the microstructure and three dimensional surface topography of coating were observed by using SEM and LSCM. Results show that as repetition rate of UIT increases, the <em>L</em><sub>cr</sub> wave acoustoelastic coefficient increases, when it reaches 300%, the <em>L</em><sub>cr</sub> wave acoustoelastic coefficient also reaches the maximum, after that the <em>L</em><sub>cr</sub> wave acoustoelastic coefficient decreases irregularly as repetition rates of UIT increases further. Compared with the <em>L</em><sub>cr</sub> wave acoustoelastic theory, when stress is in the range of turning point stress, there is a deviation on experimental result, and that deviation becomes more obvious as stress and repetition rate of UIT increase. It is analyzed that the change of microstructure, deformation state and initial stress of coating caused by UIT and different repetition rate are main reasons.</p>
physics, applied,materials science, coatings & films