Abstract:This work reports the synthesis of FeCo alloy encapsulated in N-doped carbon shell for efficient oxygen reduction reaction (ORR). The FeCoNC-0.3compound were synthesized by high temperature pyrolysis of ZIF-L with the assistance of different Fe salts (i.e., FeCl 3 ·6H 2 O, FeSO 4 ·7H 2 O, K 3 Fe(CN) 6 , Fe(NH 4 ) 2 ·(SO 4 ) 2 ·6H 2 O and (NH 4 ) 3 ·Fe(C 2 O 4 ) 3 ·3H 2 O). With the presence of FeCl 3 ·6H 2 O, FeSO 4 ·7H 2 O, Fe(NH 4 ) 2 ·(SO 4 ) 2 ·6H 2 O and (NH 4 ) 3 ·Fe(C 2 O 4 ) 3 ·3H 2 O during the pyrolysis process, FeCo alloys are formed and more nitrogen elements are remained after high temperature pyrolysis compared with that in CoNC derived from pure ZIF-L. Differently, the introduction of K 3 Fe(CN) 6 cannot lead to the generation of FeCo alloy and less nitrogen elements are remained after high temperature pyrolysis in comparison with that in CoNC. Linear relationship between the ORR onset potential and the I D /I G value of the FeCoNC-0.3compound catalysts are observed. Besides, the onset potential also increases linearly with the increase of the total content of pyridinic-N + graphitic-N + Fe(Co)-N x . These results suggest that high content of carbon defects and high content of pyridinic-N, graphitic-N and Fe(Co)- N x are beneficial for the improvement of the catalytic activities of the FeCoNC-0.3compound catalysts. Among all the as-prepared samples, FeCoNC-0.3FeCl 3 demonstrates the highest catalytic activity towards ORR due to its unique core-shell structure with a carbon layer as the shell and FeCo alloy as the core, hierarchical channels, large pore volume, high content of carbon defects and high total content of pyridine-N, graphite-N and Fe(Co)-N x . FeCoNC-0.3FeCl 3 displays an onset potential of 0.97 V and half-wave potential of 0.82 V, which are comparable to the commercial Pt/C (onset potential of 1.05 V, half-wave potential of 0.86 V). Moreover, FeCoNC-0.3FeCl 3 demonstrates much higher durability and methanol tolerance compared with Pt/C. Zn-air battery with FeCoNC-0.3FeCl 3 as the cathode catalyst demonstrates maximum power density of 105 mW cm -2 , which is close to that with Pt/C as the cathode catalyst (127 mW cm -2 ).

Improving the Catalytic Performance of Co/N/C Catalyst for Oxygen Reduction Reaction by Alloying with Fe

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Co–Fe Alloy Nanoparticles and Fe3C Nanocrystals on N-doped Biomass-Derived Porous Carbon for Superior Electrocatalytic Oxygen Reduction

Core-alloyed Shell Structured Fe@FeCo Di-Atomic Nanoclusters Loaded in Carbon Aerogels As Efficient Bi-Functional Catalysts Towards ORR and HER

A highly active and durable iron/cobalt alloy catalyst encapsulated in N-doped graphitic carbon nanotubes for oxygen reduction reaction

Enhanced Catalytic Performance of FeCoNi/N-Doped Carbon Nanospheres as Bifunctional Oxygen Catalysts

Bimetallic FeCo−N−C Catalyst for Efficient Oxygen Reduction Reaction

Effective Oxygen Reduction Reaction Performance of FeCo Alloys In Situ Anchored on Nitrogen-Doped Carbon by the Microwave-Assistant Carbon Bath Method and Subsequent Plasma Etching

Highly active CoFe alloy nanoparticles encapsulated in N-doped carbon nanostructures for oxygen reduction reaction in both alkaline and acidic media

Short nanotubular Fe-N-C catalysts with curved catalytic sites and contributing regions for oxygen reduction reaction

Adding Fe/dicyandiamide to Co-MOF to greatly improve its ORR/OER bifunctional electrocatalytic activity

Construct N -doped carbon anchored CoFe alloy nanoparticles with high content graphitic-N for electrocatalytic oxygen reduction

Well‐Combined Magnetically Separable Hybrid Cobalt Ferrite/Nitrogen‐Doped Graphene as Efficient Catalyst with Superior Performance for Oxygen Reduction Reaction

Surface-oxidized Fe–Co–Ni alloys anchored to N-doped carbon nanotubes as efficient catalysts for oxygen reduction reaction

MOF-derived Co, Fe, and Ni co-doped N-enriched hollow carbon as efficient electrocatalyst for oxygen reduction reaction

FeCo alloy encapsulated in N-doped carbon shell for efficient oxygen reduction reaction

FeCoNi alloys embedded in carbon shell as highly active catalysts towards oxygen reduction reaction

Facile Synthesis of the Amorphous Carbon Coated Fe-N-C Nanocatalyst with Efficient Activity for Oxygen Reduction Reaction in Acidic and Alkaline Media

Synthesis of hierarchically structured Fe3C/CNTs composites in a FeNC matrix for use as efficient ORR electrocatalysts

Modulating the Electronic Structure of FeCo Nanoparticles in N‐Doped Mesoporous Carbon for Efficient Oxygen Reduction Reaction

Facile synthesis of three-dimensional Co/N co-doped carbon nanocuboid for enhanced oxygen reduction reaction