Abstract:This work reports the synthesis of FeCo alloy encapsulated in N-doped carbon shell for efficient oxygen reduction reaction (ORR). The FeCoNC-0.3compound were synthesized by high temperature pyrolysis of ZIF-L with the assistance of different Fe salts (i.e., FeCl 3 ·6H 2 O, FeSO 4 ·7H 2 O, K 3 Fe(CN) 6 , Fe(NH 4 ) 2 ·(SO 4 ) 2 ·6H 2 O and (NH 4 ) 3 ·Fe(C 2 O 4 ) 3 ·3H 2 O). With the presence of FeCl 3 ·6H 2 O, FeSO 4 ·7H 2 O, Fe(NH 4 ) 2 ·(SO 4 ) 2 ·6H 2 O and (NH 4 ) 3 ·Fe(C 2 O 4 ) 3 ·3H 2 O during the pyrolysis process, FeCo alloys are formed and more nitrogen elements are remained after high temperature pyrolysis compared with that in CoNC derived from pure ZIF-L. Differently, the introduction of K 3 Fe(CN) 6 cannot lead to the generation of FeCo alloy and less nitrogen elements are remained after high temperature pyrolysis in comparison with that in CoNC. Linear relationship between the ORR onset potential and the I D /I G value of the FeCoNC-0.3compound catalysts are observed. Besides, the onset potential also increases linearly with the increase of the total content of pyridinic-N + graphitic-N + Fe(Co)-N x . These results suggest that high content of carbon defects and high content of pyridinic-N, graphitic-N and Fe(Co)- N x are beneficial for the improvement of the catalytic activities of the FeCoNC-0.3compound catalysts. Among all the as-prepared samples, FeCoNC-0.3FeCl 3 demonstrates the highest catalytic activity towards ORR due to its unique core-shell structure with a carbon layer as the shell and FeCo alloy as the core, hierarchical channels, large pore volume, high content of carbon defects and high total content of pyridine-N, graphite-N and Fe(Co)-N x . FeCoNC-0.3FeCl 3 displays an onset potential of 0.97 V and half-wave potential of 0.82 V, which are comparable to the commercial Pt/C (onset potential of 1.05 V, half-wave potential of 0.86 V). Moreover, FeCoNC-0.3FeCl 3 demonstrates much higher durability and methanol tolerance compared with Pt/C. Zn-air battery with FeCoNC-0.3FeCl 3 as the cathode catalyst demonstrates maximum power density of 105 mW cm -2 , which is close to that with Pt/C as the cathode catalyst (127 mW cm -2 ).

Co–Fe Alloy Nanoparticles and Fe3C Nanocrystals on N-doped Biomass-Derived Porous Carbon for Superior Electrocatalytic Oxygen Reduction

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Highly active CoFe alloy nanoparticles encapsulated in N-doped carbon nanostructures for oxygen reduction reaction in both alkaline and acidic media

Fe3C cluster-promoted single-atom Fe, N doped carbon for oxygen-reduction reaction

Improving the Catalytic Performance of Co/N/C Catalyst for Oxygen Reduction Reaction by Alloying with Fe

Prussian blue analogues derived iron-cobalt alloy embedded in nitrogen-doped porous carbon nanofibers for efficient oxygen reduction reaction in both alkaline and acidic solutions

Co3O4 Nanoparticle-Decorated N-Doped Mesoporous Carbon Nanofibers as an Efficient Catalyst for Oxygen Reduction Reaction

Porous Core-Shell Fe3C Embedded N-doped Carbon Nanofibers as an Effective Electrocatalysts for Oxygen Reduction Reaction

A highly active and durable iron/cobalt alloy catalyst encapsulated in N-doped graphitic carbon nanotubes for oxygen reduction reaction

Effective Oxygen Reduction Reaction Performance of FeCo Alloys In Situ Anchored on Nitrogen-Doped Carbon by the Microwave-Assistant Carbon Bath Method and Subsequent Plasma Etching

Construct N -doped carbon anchored CoFe alloy nanoparticles with high content graphitic-N for electrocatalytic oxygen reduction

Scalable Synthesis of N–Doped Graphene–Oxide–Supported FeCo(OH)x Nanosheets for Efficient Co–Doped Fe3O4 Nanoparticle-Based Oxygen Reduction Reaction Electrocatalysis

MOF-derived Co, Fe, and Ni co-doped N-enriched hollow carbon as efficient electrocatalyst for oxygen reduction reaction

Self-Templating Synthesis of N/P/Fe Co-Doped 3D Porous Carbon for Oxygen Reduction Reaction Electrocatalysts in Alkaline Media

Rational design of Fe, N co-doped porous carbon derived from conjugated microporous polymer as an electrocatalytic platform for oxygen reduction reaction

FeCo alloy encapsulated in N-doped carbon shell for efficient oxygen reduction reaction

Bimetallic FeCo−N−C Catalyst for Efficient Oxygen Reduction Reaction

Modulating the Electronic Structure of FeCo Nanoparticles in N‐Doped Mesoporous Carbon for Efficient Oxygen Reduction Reaction

A high-performance nitrogen-rich ZIF-8-derived Fe-Co-NC electrocatalyst for the oxygen reduction reaction

Achieving efficient oxygen reduction on ultra-low metal-loaded electrocatalysts by constructing well-dispersed bimetallic sites and interconnected porous channels

ChemInform Abstract: Iron Carbide Nanoparticles Encapsulated in Mesoporous Fe‐N‐Doped Carbon Nanofibers for Efficient Electrocatalysis.