Effect of cation doping on the electrochemical properties of Li2MoO3 as a promising cathode material for lithium-ion battery
Rui Teng,Hai-Tao Yu,Chen-Feng Guo,Xiao-dong Wang,Ying-Jie Qiao,Ying Xie,Ting-Feng Yi
DOI: https://doi.org/10.1007/s11581-020-03607-4
IF: 2.961
2020-05-30
Ionics
Abstract:<p class="a-plus-plus">A series of cation-doped Li<sub class="a-plus-plus">2</sub>MoO<sub class="a-plus-plus">3</sub> materials were successfully prepared by a facile method. The experimental characterizations showed that the incorporation of metal cations can change the structures of Li<sub class="a-plus-plus">2</sub>MoO<sub class="a-plus-plus">3</sub> materials. In addition, Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>M<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub> materials have higher structural stabilities and electrical conductivities in comparison to the pristine sample, which results in a much improved electrochemical performance. The initial discharge capacities are respectively 246.87, 256.92, 255.38, 271.12, and 261.25 mAh g<sup class="a-plus-plus">−1</sup> for Li<sub class="a-plus-plus">2</sub>MoO<sub class="a-plus-plus">3</sub>, Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>Zn<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub>, Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>Mg<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub>, Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>Cr<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub>, and Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>La<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub>. Li<sub class="a-plus-plus">2</sub>Mo<sub class="a-plus-plus">0.96</sub>La<sub class="a-plus-plus">0.04</sub>O<sub class="a-plus-plus">3</sub> has the best performance, and it can deliver a specific capacity of 149.89 mAh g<sup class="a-plus-plus">−1</sup> at the 50th cycle at a charge/discharge current density of 34 mA g<sup class="a-plus-plus">−1</sup>. Our experiments have identified the promising role of cation doping and offered some important information for the design and optimization of Li<sub class="a-plus-plus">2</sub>MoO<sub class="a-plus-plus">3</sub>-based cathode materials.</p>
chemistry, physical,physics, condensed matter,electrochemistry