Abstract:In order to explore the occurrence area of pervious concrete freeze-thaw deterioration, the mass loss, strength deterioration, ultrasonic longitudinal wave velocity and dynamic elastic modulus attenuation of pervious concrete under freeze-thaw cycles were measured, and a prediction model of freeze-thaw damage was established. The mechanical properties of hardened cement pastes with the same W/C ratio under freeze-thaw cycles were also measured. Mercury intrusion porosimetry (MIP) was used to measure the pore structure characteristic parameters and pore size distribution changes of cement paste under freeze-thaw cycle, and the microstructure evolution of interfacial transition zone (ITZ) of paste and aggregate was observed by SEM scanning electron microscopy. Finally, a pervious concrete model was established by DEM to analyze the relationship between the number of freeze-thaw cycles and the mesoscopic parameters. The results indicated that the quality, strength and dynamic elastic modulus of pervious concrete deteriorate to different degrees under the conditions of water freezing and salt freezing. The damage sensitivity and strength loss of freeze-thaw damage is greater than the dynamic elastic modulus loss, which is greater than mass loss. In the pervious concrete paste which underwent 100 freeze-thaw cycles, the pore structure and macro strength had no obvious change, and hardened paste and the aggregate-interface-generated defects increased with the increase in freezing and thawing times, indicating that the deterioration of pervious concrete performance under freeze-thaw cycles was closely related to the deterioration of the interface strength of the aggregate and hardened paste. The pervious concrete model established by DEM can accurately simulate the change of the compressive modulus and the strength of pervious concrete during freeze-thaw cycles.

RETRACTED: The evolution of structure properties of vegetation concrete under freeze–thaw cycles

Effects of freeze-thaw cycling on the engineering properties of vegetation concrete

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Effect of Different Moisture Content on Mechanical Parameters of Red Clay Under Freeze-Thaw Cycle

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Impact of Wetting and Drying Cycles on the Mechanical Properties and Microstructure of Vegetation-growing Concrete

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Behavior of PVA fiber concrete under freezing and thawing cycles

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

Study on pore structure and the mechanical properties of sandstone-concrete binary under freeze-thaw environment

Effect of freeze‒thaw cycles on root–Soil composite mechanical properties and slope stability

Experimental studies on mechanical properties of concrete under freeze-thaw action

Degradation of mechanical properties of concrete caused by freeze-thaw action

Freeze–Thaw Damage Characteristics of Concrete Based on Compressive Mechanical Properties and Acoustic Parameters

Microstructural Damage Evolution And Its Effect On Fracture Behavior Of Concrete Subjected To Freeze-Thaw Cycles

Stress-strain relationship of concrete in freeze-thaw environment

Effect of freeze-thaw cycles on mechanical behavior of clay-gravel mixtures

Investigation of creep characteristics and microscopic mechanism of cemented-soil subjected to freeze-thaw

Investigating Mechanical Properties of Cemented Soil under Static and Dynamic Loading after a Freeze-Thaw Cycle

Behavior of Air-Entrained Concrete after Freeze-Thaw Cycles