Abstract:The purpose of this paper was to determine the influence of selected parameters of Direct Metal Laser Sintering and various heat treatment temperatures on the mechanical properties of Ti6Al4V samples oriented vertically (V, ZX) and horizontally (H, XZ). The performed micro-CT scans of as-build samples revealed that the change in laser energy density significantly influences the change in porosity of the material, which the parameters (130–210 W; 300–1300 mm/s), from 9.31% (130 W, 1300 mm/s) to 0.16% (190 W, 500 mm/s) are given. The mechanical properties, ultimate tensile strength (UTS, Rm) and yield strength (YS, Re) of the DMLS as-build samples, were higher than the ASTM F 1472 standard suggestion (UTS = 1100.13 ± 126.17 MPa, YS = 1065.46 ± 127.91 MPa), and simultaneously, the elongation at break was lower than required for biomedical implants (A = 4.23 ± 1.24%). The low ductility and high UTS were caused by a specific microstructure made of α’ martensite and columnar prior β grains. X-Ray Diffraction (XRD) analysis revealed that heat treatment at 850 °C for 2 h caused the change of the microstructure intothe α + β combination, affecting the change of strength parameters—a reduction of UTS and YS with the simultaneous increase in elongation (A). Thus, properties similar to those indicated by the standard were obtained (UTS = 908.63 ± 119.49 MPa, YS = 795.9 ± 159.32 MPa, A = 8.72 ± 2.51%), while the porosity remained almost unchanged. Moreover, the heat treatment at 850 °C resulted in the disappearance of anisotropic material properties caused by the layered structure (UTSZX = 908.36 ± 122.79 MPa, UTSXZ = 908.97 ± 118.198 MPa, YSZX = 807.83 ± 124.05 MPa, YSXZ = 810.56 ± 124.05 MPa, AZX = 8.75 ± 2.65%, and AXZ = 8.68 ± 2.41%).

Factors Influencing the Corrosion Behavior of Direct Metal Laser Sintered Ti-6Al-4V for Biomedical Applications

Microstructural evolution and corrosion behavior of Ti–6Al–4V alloy fabricated by laser metal deposition for dental applications

Effect of Laser Sintering Parameters on the Microstructure, Mechanical Properties and Corrosion Behavior of Titanium Grade 5 Alloy

Mechanical Properties and Microstructure of DMLS Ti6Al4V Alloy Dedicated to Biomedical Applications

Microstructure and Electrochemical Behavior of a 3D-Printed Ti-6Al-4V Alloy

Electrochemical Corrosion Behavior and Mechanical Response of Selective Laser Melted Porous Metallic Biomaterials

Mechanical properties, corrosion behavior and cytotoxicity of Ti-6Al-4V alloy fabricated by laser metal deposition

Microstructure and electrochemical corrosion behavior of selective laser melted Ti−6Al−4V alloy in simulated artificial saliva

Effect of Laser Energy Density, Internal Porosity and Heat Treatment on Mechanical Behavior of Biomedical Ti6Al4V Alloy Obtained with DMLS Technology

Design and Characterization of Selective Laser‐melted Ti6Al4V–5Cu Alloy for Dental Implants

Microstructure and Corrosion Resistance of Ti6Al4V Manufactured by Laser Powder Bed Fusion

A comparative study of surface characterization and corrosion behavior of micro-arc oxidation treated Ti–6Al–4V alloy prepared by SEBM and SLM

Tribological Behavior of Direct Metal Laser Sintering–Manufactured Ti6Al4V Alloy in Different Biofluids for Orthopedic Implants

Mechanical and Electrochemical Corrosion Behaviors of Porous Ti-6Al-4V Alloys Prepared by an Electrochemical Sintering Approach

Laser surface modification of Ti--6Al--4V: wear and corrosion characterization in simulated biofluid

Study on corrosion behavior of the selective laser melted NiTi alloy with superior tensile property and shape memory effect

Comparison on the Electrochemical Corrosion Behavior of Ti6Al4V Alloys Fabricated by Laser Powder Bed Fusion and Casting

Microstructural, mechanical and in vitro biological properties of Ti6Al4V-5Cu alloy fabricated by selective laser melting

Corrosion fatigue behavior of porous Cu-bearing Ti alloy fabricated by selective laser melting

Corrosion Resistance of Selective Laser Melted Ti6Al4V3Cu Alloy Produced Using Pre-Alloyed and Mixed Powder

Effect of electropolishing on mechanical property enhancement of Ti6Al4V porous materials fabricated by selective laser melting