Abstract:This research attempts to create a pressure-sensitive adhesive (PSA) from cardanol as an outset material. The two kinds of formulations were established; the first scheme followed the epoxidation of cardanol, dihydroxylation, and PSA development. In the latter system, cardanol was pretreated with dichlorodimethysilane (DCDMS) in the second scheme, continuing the same procedure to obtain PSA resin. The chemical nature and structure confirmation were done using FTIR and NMR spectroscopy, hydroxyl value, epoxy equivalent weight (EEW), etc. To evaluate PSA resin's crystallinity, thermal stability and hydrophilicity the film was separately obtained for both the schemes by curing whereas to obtain PSA tapes the obtained PSA and tackifying resins were applied onto PET sheets. XRD analysis showed a decrease in the degree of crystallinity after incorporating DCDMS. The gel content values decreased, whereas the water absorption values increased, which could be related to the increase in the hydrophilic nature of PSA with an increasing number of tacky sites. TGA and DSC showed the formation of a high amount of char yield (∼31%) and a higher Tg (−37.72 °C) in Si containing film. The probe tack, peel strength, and shear strength values were high for the formulation with equal amounts of PSA and tackifying resin. Finally, the contact angle measurements showed that the hydrophobicity of film was also improved after incorporating DCDMS. The materials resembling PSA tape and including only small amounts of tackifying resins and crosslinkers displayed the ideal characteristics with satisfactory results.

Developments in pressure-sensitive adhesives: a review

Surface Enrichment by Conventional and Polymerizable Sulfated Nonylphenol Ethoxylate Emulsifiers in Water-Based Pressure-Sensitive Adhesive

Water‐soluble/dispersible Cationic Pressure‐sensitive Adhesives. II. Adhesives from Emulsion Polymerization

New Chemistries for Degradable Pressure‐Sensitive Adhesive Networks

Development of organic silicon pressure-sensitive adhesive

Sticky Architecture: Encoding Pressure Sensitive Adhesion in Polymer Networks

Designing Acrylic Latexes for Pressure Sensitive Adhesives: A review

Research Advancement in Pressure-Sensitive Adhesives

Development of cardanol-derived epoxidized and Si-modified pressure-sensitive adhesives (PSAs)

Research progress of acrylate pressure sensitive adhesives

Research Progress of Polyurethane Pressure-Sensitive Adhesive

Development of solvent-based polyacrylate pressure sensitive adhesives

Silanization as a strategy to design polyurethane-acrylic hybrid pressure-sensitive adhesives

Pressure Sensitive Adhesive Tape: A Versatile Material Platform for Optical Sensors

Research advances of vegetable oil based pressure sensitive adhesives

Synthesis and Characterization of Pressure-Sensitive Adhesives Based on a Naphthyl Curing Agent

Research Progress of Waterborne Acrylate Pressure-Sensitive Adhesive

Novel Acrylic Pressure-Sensitive Adhesive (psa) Containing Silver Particles

Pressure-Sensitive Adhesive with Enhanced and Phototunable Underwater Adhesion.

Present Situation of Application and Development of Hot- Melt Pressure Sensitive Adhesives

Isosorbide-Based Acrylic Pressure-Sensitive Adhesives Through UV-Cured Crosslinking with a Balance Between Adhesion and Cohesion