Non-affinity in multi-material mechanical metamaterials

M. J. Mirzaali,H. Pahlavani,E. Yarali,A. A. Zadpoor

DOI: https://doi.org/10.1038/s41598-020-67984-6

IF: 4.6

2020-07-13

Scientific Reports

Abstract:Abstract Non-affine deformations enable mechanical metamaterials to achieve their unusual properties while imposing implications for their structural integrity. The presence of multiple phases with different mechanical properties results in additional non-affinity of the deformations, a phenomenon that has never been studied before in the area of extremal mechanical metamaterials. Here, we studied the degree of non-affinity, $$\Gamma $$ Γ , resulting from the random substitution of a fraction of the struts, $${\rho }_{h}$$ ρ h , that make up a lattice structure and are printed using a soft material (elastic modulus = $${E}_{s}$$ E s ) by those printed using a hard material ( $${E}_{h}$$ E h ). Depending on the unit cell angle (i.e., $$\theta $$ θ = 60°, 90°, or 120°), the lattice structures exhibited negative, near-zero, or positive values of the Poisson’s ratio, respectively. We found that the auxetic structures exhibit the highest levels of non-affinity, followed by the structures with positive and near-zero values of the Poisson’s ratio. We also observed an increase in $$\Gamma $$ Γ with $$\frac{{E}_{h}}{{E}_{s}}$$ E h E s and $${\rho }_{h}$$ ρ h until $$\frac{{E}_{h}}{{E}_{s}}$$ E h E s =10 4 and $${\rho }_{h}$$ ρ h = 75%-90% after which $$\Gamma $$ Γ saturated. The dependency of $$\Gamma $$ Γ upon $${\rho }_{h}$$ ρ h was therefore found to be highly asymmetric. The positive and negative values of the Poisson’s ratio were strongly correlated with $$\Gamma $$ Γ . Interestingly, achieving extremely high or extremely low values of the Poisson’s ratio required highly affine deformations. In conclusion, our results clearly show the importance of considering non-affinity when trying to achieve a specific set of mechanical properties and underscore the structural integrity implications in multi-material mechanical metamaterials.

multidisciplinary sciences