Abstract:<p>This study demonstrates that a combined precompression and subsequent annealing (PCA) treatment considerably improves the damping capacity of extruded pure Mg. Variations in the microstructure and damping capacity with the annealing temperature of PCA are investigated. Precompression along the extrusion direction induces an increase in the dislocation density and the formation of numerous {10–12} twins, the latter of which results in significant lattice reorientation and an increased total boundary length. Subsequent annealing at 200 °C causes barely any change in the formed twin structure, whereas annealing above 250 °C induces extensive grain growth through strain-induced grain boundary migration; this consequently reduces the twin fraction and dislocation density and increases the grain size. The samples subjected to PCA show higher damping capacities than the initial sample in both low- and high-strain-amplitude regions. The improved damping capacity in the low-strain-amplitude region is due primarily to the increase in the dislocation density and Schmid factor for basal slip; namely, more abundant dislocations move more readily, which leads to dissipation of a larger amount of energy via the vibration and sweeping motion of dislocations. In the high-strain-amplitude region, a large sweeping motion of dislocations within grown grains and additional sweeping motion of twin boundaries within twinned grains significantly improve the damping capacity. However, PCA treatment with annealing at 200 °C causes a relatively smaller increment in the damping capacity in the high-strain-amplitude region because the excessive dislocations and twin boundaries in this sample hinder their motions.</p>

Change in damping capacity arising from twin-boundary segregation in solid-solution magnesium alloys

Change in Damping Capacity Due to Twin Boundary Segregation in Solid Solution Magnesium Alloys

Enhanced damping capacity of magnesium alloys by tensile twin boundaries

Atomic simulations of the effect of Y and Al segregation on the boundary characteristics of a double twin in Mg

Solute Segregation and Pinning Effect on Lateral Twin Boundary in Magnesium

Effect of alloying elements and heat treatment on damping capacity of Mg-Al alloys.

Improvement in damping capacity of extruded pure magnesium through precompression and subsequent annealing: Effects of dislocation and twin boundary motions

A Study on the Damping Capacities of Mg–Zn–Y-Based Alloys with Lamellar Long Period Stacking Ordered Phases by Preparation Process

The Hydriding and Dehydriding Properties of Some Multicomponent Rare-Earth Magnesium Alloys

Temperature Damping Capacity and Microstructure Evolution of Mg–Al–Zn–Sn Alloy

Evolution of the Microstructure and Microsegregation in Subrapidly Solidified Mg–6Al–4Zn–1.2Sn Magnesium Alloy

Solid solution strengthening and damping capacity of Mg−Ga binary alloys

A Transmission Electron Microscopy Investigation of Defects in an Mg-Cu-Mn-Zn-Y Damping Alloy

Effect of Aluminum Concentration on Damping Capacity during Annealing in AZ-Series Magnesium Alloy

Twin-solute, twin-dislocation and twin-twin interactions in magnesium

Effect of Recrystallization Behavior of AZ31 Magnesium Alloy on Damping Capacity

The ultrahigh damping capacity of Mg-Sn-Y alloy

Anomalous Hardening in Magnesium Driven by a Size-Dependent Transition in Deformation Modes

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

Effect of Calcium on the Rate of Grain Boundary Migration in Pure Magnesium During Annealing

The Dislocation-Twin Interaction and Evolution of Twin Boundary in AZ31 Mg Alloy