Large-size carbon-coated SnO2 composite as improved anode material for lithium ion batteries

Wenhe Xie,Wenjie Wang,Zijun Xu,Wenrui Zheng,Hongwei Yue,Chunlei Wang,Chao Zhang,Haibin Sun

DOI: https://doi.org/10.1007/s11581-020-03764-6

IF: 2.961

2020-09-09

Ionics

Abstract:<p class="a-plus-plus">SnO<sub class="a-plus-plus">2</sub> microbelt coating carbon composite was fabricated via electrospinning precursor, thermal treatment, and polymer adhesion process. Primarily, the solvent of electrospinning jet quickly evaporates in a relatively high-temperature environment; intermediate microtubules simultaneously form when the solute containing tin salt and binder converge on the skin of the jet; then, the microtubules collapse into flat microbelt product under the action of atmospheric pressure. Subsequently, SnO<sub class="a-plus-plus">2</sub> microbelts can be obtained by annealing the electrospinning products. Finally, the SnO<sub class="a-plus-plus">2</sub>@C microbelts are synthesized by dopamine polymerization and carbonization process. The SnO<sub class="a-plus-plus">2</sub>@C microbelts present a regular strip with width ~ 1.2 μm and thickness ~ 120 nm. Because of the synergy effect of carbon coating and SnO<sub class="a-plus-plus">2</sub> microbelt design project, the composite shows superior lithium storage of 504 mAh g<sup class="a-plus-plus">-1</sup> after 100 cycles at 0.2 A g<sup class="a-plus-plus">-1</sup>. The SnO<sub class="a-plus-plus">2</sub>@C microbelts are expected to be competitive alternative anode material of next-generation LIBs.</p>

chemistry, physical,physics, condensed matter,electrochemistry