Carbon-coated SnO x anchored on phosphorus-doped carbon framework as high performance anode of lithium-ion batteries
Xue Zhang,Haoran Xu,Huanhuan Liu,Wenzhao Ma,Dapeng Wu,Zhaohui Meng,Lijuan Wang
DOI: https://doi.org/10.1016/j.ceramint.2023.11.114
IF: 5.532
2023-12-10
Ceramics International
Abstract:SnO 2 has been recognized as one of the most potential anodes of lithium-ion batteries due to its high theoretical specific capacity, low cost, simple synthetic method, and environmental friendliness. However, the application of SnO 2 is hindered owing to its huge volume expansion (∼300 %) and poor electronic conductivity. In this work, carbon-coated SnO x containing some SnO anchored on the phosphorus-doped carbon framework (SnO x /C–P@C) has been fabricated via a novel, simple and green precipitation route using phytic acid as the complexing agent, carbon and phosphorus sources, and glucose as the second carbon source. Phosphorus-doped carbon framework in situ forms via calcining phytic acid at a high temperature. Phosphorus doping can further enhance the electronic conductivity of carbon. The carbon framework can provide sufficient buffer space to make the SnO x particles have good dispersion. The carbon layer from glucose can prevent the direct contact between SnO x and the electrolyte to decrease the side reactions and then reinforce the structure of SnO x /C–P@C. The synergistic effect of the double carbon effectively controls the volume expansion, enhances the electronic conductivity and diffusion coefficient of Li + ions as well as capacitive contribution ratio, and reduces the charge transfer resistance of SnO x /C–P@C. The SnO x /C– sample with the carbon content of 25.8 wt% exhibits outstanding electrochemical performance. At 0.1 A g −1 , the discharge specific capacity of 776.2 mAh g −1 can be reached after 100 cycles. At 0.5 A g −1 , 555.5 mAh g −1 is still delivered after 200 cycles. Moreover, the sample shows good potential practical applications in the LiNi 0.5 Mn 1.5 O 4 //SnO x /C– full cell. 687.9, 597.1, 510.1, 434.8 and 595.6 mAh g −1 are retained for the full cell at 0.1, 0.2, 0.5, 1 and 0.1 C, respectively. The full cell cycling for 200 cycles at 0.5 C can still light up the light-emitting diode (LED) bulbs.
materials science, ceramics