Abstract:This work presents the experimental results of narrow gap butt welding of steel plates with large thickness by using the Metal Active Gas (MAG) welding method.The typical defects are accompanied with this process such as the infusion in the side wall and the porosity due to the narrow gap which affect on the melting process. Thus, some publications noted the results of welding for the thickness up to 20−30 mm and the chamfer angle about 30° using GMAW/MIG, GTAW/TIG, SMAW and new development such as laser – arc hybrid, laser multi- pass technique, super -TIG welding etc. But the production requires the solution to save the costs by the reduction of time, labour and investment keeping the standard quality. That is the aim of this study. In order to improve the quality of weld joint and increase the productivity of the process, is it suggested to develop the innovative welding process, in which the welding voltage – Uw, the translational velocity of the tip – Vt, and rotational velocity of the tip – Vr, are changing. This helped to increase the thickness of steel plates up to 50 mm and the chamfer angle decreased at 15°, providing the satisfied quality of the weld. The micrography study serve as the preliminary proof of this hypothesis. The microstructures in 4 regions, such as the weld center zone, heat-affected zone (HAZ), parent metal region, and the boundary between the weld metal and the HAZ were examined. The microstructures of 13 positions from different experiments are investigated using the optical microscope (Axiovert 25).These experiments covered all specific points (node) locating accordingly to three layers from bottom to top of the weld joint . The findings proved the welding quality is similar in case of narrow gap but the chamfer angle is twice lower and the thickness is increased. The result of the study enhances the productivity due to saving the labour cost and the welding materials. It is recommended to consider the effect of other factors (such as cooling conditions, dwell time when the arc approaching the side walls) to optimize the weld quality. There is the huge volume of the heavy steel constructions with the thick steel construction and specific narrow gap in industry. The results of this study with the optimization and more deeper evaluation the influence of main parameters of welding process to eliminate the typical defects will be the valuable reco mmendation for the managers and engineers in the production of metallic constructions

High-Efficiency and Low-Heat-Input CO2 Arc-Welding Technology for Butt Joint of Thick Steel Plate Using Hot Wire

Optimization of welding conditions for hot-wire GMAW with CO2 shielding on heavy-thick butt joint

Selection of Welding Conditions for Achieving Both a High Efficiency and Low Heat Input for Hot-Wire Gas Metal Arc Welding

Improve the Manufacturing Efficiency of Steel Bars by Using Hot-Wire Pulse Arc Additive Manufacturing

Improving mechanical strength and isotropy for wire-arc additive manufactured 304L stainless steels via controlling arc heat input

Narrow-gap Laser Welding Using Filler Wire of Thick Steel Plates

Arc Heating Hot Wire Assisted Arc Welding Technique for Low Resistance Welding Wire

Thick-wire GMAW for fusion welding of high-strength steels

Study and Application of Process Performance and Welding Wire of CO2 Welding and MAG Welding

The evaluation on performance of narrow- gap welding thick steel plates under the influence of main welding parameters

Feasibility study on tandem narrow gap GMAW of 65 mm thick steel plate

Study on multipass welding of thick section steels using CO2 laser welding

Butt welding and measurement system of twin-wire submerged arc welding of thick A105 steel plate

High-speed hot-wire laser brazing technology for steel/aluminum alloy dissimilar joint using twin beam irradiation

Multipass welding of thick section steels using autogenous CO2 laser welding and CO2 laser-MIG hybrid welding

Investigation of Process Stability and Weld Quality of Underwater Wet Flux-Cored Arc Welding of Low-Alloy High-Strength Steel with Oxy-Rutile Wire

A novel high efficiency narrow-gap laser welding technology of 120 mm high-strength steel

Performance optimization and investigation of metal-cored filler wires for high-strength steel during gas metal arc welding

Bead shape control in high-speed fillet welding using hot-wire GMA laser hybrid welding technology

Experimental Investigation of Additive Manufacturing Using a Hot-Wire Plasma Welding Process on Titanium Parts

A Study on the Mechanisms of the CWW SAW Process