Calcium ion pinned vanadium oxide cathode for high-capacity and long-life aqueous rechargeable zinc-ion batteries

Min Du,Feng Zhang,Xiaofei Zhang,Wentao Dong,Yuanhua Sang,Jianjun Wang,Hong Liu,Shuhua Wang

DOI: https://doi.org/10.1007/s11426-020-9830-8

2020-10-22

Science China Chemistry

Abstract:<p class="a-plus-plus">Rechargeable aqueous zinc ion batteries (ZIBs), with the easy operation, cost effectiveness, and high safety, are emerging candidates for high-energy wearable/portable energy storage systems. Unfortunately, the unsatisfactory energy density and undesired long-term cycling performance of the cathode hinder the development of ZIBs. Here, we report the chemical pre-intercalation of a small amount of calcium ions into V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> as the cathode material. The cathode of Ca<sub class="a-plus-plus">0.04</sub>V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>•1.74H<sub class="a-plus-plus">2</sub>O (CVO) was demonstrated to have a high specific capacity of 400 mA h g<sup class="a-plus-plus">−1</sup> at the current density of 0.05 A g<sup class="a-plus-plus">−1</sup> and 187 mA h g<sup class="a-plus-plus">−1</sup> at 10 A g<sup class="a-plus-plus">−1</sup>, along with impressive capacity retention (100% capacity retention at 10 A g<sup class="a-plus-plus">−1</sup> for 3,000 cycles). Meanwhile, the CVO// Zn battery exhibits a high energy density of 308 Wh kg<sup class="a-plus-plus">−1</sup> and a power density of 467 W kg<sup class="a-plus-plus">−1</sup> at 0.5 A g<sup class="a-plus-plus">−1</sup>. The superior performance originates from the pinning effect of the calcium ions and the lubricating effect of the structural water. The energy storage mechanism of the CVO cathode was also investigated in detail. The new phase (Zn<sub class="a-plus-plus">3</sub>(OH)<sub class="a-plus-plus">2</sub>V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">7</sub>•2H<sub class="a-plus-plus">2</sub>O) generated upon cycling participates in the electrochemical reaction and thus contributes to the excellent electrochemical performance. The small amount of Ca<sup class="a-plus-plus">2+</sup> pre-inserted into the interlayer of V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> sheds light on constructing cathodes with high energy density for ZIBs.</p>

chemistry, multidisciplinary