Effect of Fluid parameters on Erosion-corrosion behavior of Al- 2%Zn coatings on AA5083 Aluminium Alloy in 3.5% NaCl

Yanming Xia,

DOI: https://doi.org/10.20964/2022.04.03

IF: 1.541

2022-04-01

International Journal of Electrochemical Science

Abstract:The erosion-corrosion behavior of Al-2%Zn coating in flowing 3.5% NaCl solution was investigated by using potentiodynamic polarization, electrochemical impedance spectroscopy and surface analysis techniques through a self-made impingement jet device. The results show that the corrosion process of the coating in a static solution is controlled by activation and mass transfer processes. In flowing solutions with or without sand, corrosion of the coating is an activation-controlled process. The flowing solution will accelerate the oxygen transfer process, resulting in a decrease in the cathodic Tafel slope and an increase in cathodic current density. Due to the rough surface of the coating, the direct impact of the fluid will destroy the corrosion product film, resulting in an increase in anodic current density. Sand particles mainly play a role in the erosion and destruction of the surface oxide film layer. Cu2+ ions and Hg2+ ions have a similar effect, as their concentration increases, the oxygen reduction reaction at cathode is weakened, so is the amount of oxide generated on the surface. Eventually, an increase in anodic current density and a negative shift in potential can be observed. Sand, Cu2+ ions and Hg2+ ions play a positive synergistic role in the erosion-corrosion process of the coating in the flowing 3.5% NaCl.

electrochemistry