Manipulating Exciton Transfer between Colloidal Quantum Dots and Graphene Oxide

Ruixiang Wu,Xiaojun Guo,Jingjing Luo,Xiangyang Miao,Junfeng Zhang

DOI: https://doi.org/10.1021/acs.jpcc.0c06242

2020-11-02

The Journal of Physical Chemistry C

Abstract:Colloidal quantum dots and graphene oxide composite are promising semiconductor nanomaterials for optoelectronic devices due in part to their tunable light absorption and extraordinary carrier transport properties. We investigate the exciton interaction between them during laser irradiation by transient absorption spectroscopy. In the transient measurement, an exciton bleach buildup signal is exhibited before its recovery at the long probe wavelength. It can be attributed that the trapped electron of graphene oxide backward transfers to the conduction band of quantum dots. With the reduction degree of graphene oxide being increased by laser irradiation, backward electron transfer would take place at both longwave and shortwave, resulting in a broader and stronger exciton bleach feature. Subsequently, exciton bleach disappeared at longwave because of hole trapping by graphene oxide. Exciton transfer of quantum dots and graphene oxide composite has been efficiently manipulated by laser irradiation.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.jpcc.0c06242?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.jpcc.0c06242</a>.SEM image displays a GO microsheet structure (Figure S1); TA spectra as a function of the probe wavelength for the QD-GO composite with the irradiation time is increased gradually (Figure S2); fitting curves of the TA kinetic trajectory with two different functions (Figure S3): (a) pseudocolor TA plot of colloidal QDs (0.84 mg/mL) under laser excitation of 355 nm and (b) TA kinetic trajectory of QDs at 642 nm (Figure S4); emission spectra and absorption spectra of the QD-GO composite at the excitation of 355 nm with irradiation time are increased gradually (Figure S5); and two-peak fitting of D and G bands in the Raman spectrum of GO with the integrated area values (<i>I</i>_D/<i>I</i>_G) of D and G peaks being 1.25 (Figure S6) (<a class="ext-link" href="/doi/suppl/10.1021/acs.jpcc.0c06242/suppl_file/jp0c06242_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.