Effect of Rhodium Modification on Activity of Platinum Nanoparticle-Loaded Carbon Catalysts for Electrochemical Toluene Hydrogenation

Toyoki Imada,Masanobu Chiku,Eiji Higuchi,Hiroshi Inoue

DOI: https://doi.org/10.1021/acscatal.0c04179

IF: 12.9

2020-11-10

ACS Catalysis

Abstract:Toluene (TL)/methylcyclohexane (MCH) is an attractive organic hydride couple for secure storage and transportation of large amounts of hydrogen. Electrochemical hydrogenation of TL to MCH can achieve energy savings compared with hydrogenation using molecular hydrogen generated separately, and catalyst development to improve the kinetics of electrochemical TL hydrogenation is imperative. Here, we found that using rhodium to modify Pt nanoparticles (NPs) supported on carbon black (Pt/C) significantly improved the kinetics of electrochemical TL hydrogenation despite rhodium as a single catalyst being less active than platinum. Rhodium was deposited on Pt NPs by reducing Rh³⁺ ions with molecular hydrogen. By optimizing the CO-stripping conditions, the electrochemical surface areas (ECSAs) of Pt and Rh for Rh-deposited Pt NP-loaded carbon (Rh<i>_x</i>/Pt/C) catalysts were individually determined, and the Rh coverage (θ_Rh) and the ratio of ECSA of the deposited Rh to the total ECSA (<i>F</i>_Rh) were successfully estimated. θ_Rh increased with the Rh/Pt mole ratio for Rh<i>_x</i>/Pt/C and then plateaued around 0.20, whereas <i>F</i>_Rh still increased. According to linear sweep voltammograms and Tafel plots, the Rh<i>_x</i>/Pt/C electrodes exhibited peak hydrogenation activity 2.7 times that of the Pt/C electrode, and addition of H_ads to TL was rate-determining. Increased θ_Rh facilitated the addition of H_ads generated on Rh to TL adsorbed on Pt at the extended interface between Rh and Pt, leading to increased geometric reduction current density at 0 V vs RHE (<i>j</i>_geo,0). Plateauing of θ_Rh was accompanied by plateauing of <i>j</i>_geo,0, attributed to a lack of any further increase in the extent of the interface. In the electrochemical hydrogen pump hydrogenation of 30 vol % TL with the Rh<i>_x</i>/Pt/C electrodes, MCH was the sole TL hydrogenation product. After the conversion of TL to MCH exceeded about 85%, the hydrogen evolution reaction became appreciable, occurring significantly later than with the Pt/C electrode.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c04179?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c04179</a>.A schematic diagram of electrochemical hydrogen pump TL hydrogenation system, cyclic voltammograms of Pt and Rh electrodes, and various parameters for Rh<i>_x</i>/Pt/C electrodes (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c04179/suppl_file/cs0c04179_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, physical