Amorphous MoOx with high oxophilicity interfaced with PtMo alloy nanoparticles boosts anti‐CO hydrogen electrocatalysis
Heng Luo,Kai Wang,Fangxu Lin,Fan Lv,Jinhui Zhou,Weiyu Zhang,Dawei Wang,Wenshu Zhang,Qinghua Zhang,Lin Gu,Mingchuan Luo,Shaojun Guo
DOI: https://doi.org/10.1002/adma.202211854
IF: 29.4
2023-02-04
Advanced Materials
Abstract:Advancing electrocatalysts for alkaline hydrogen oxidation/evolution reaction (HOR/HER) is essential for anion exchange membrane‐based devices. The state‐of‐the‐art Pt‐based electrocatalysts for alkaline HOR are suffering from low intrinsic activities and severe CO poisoning due to challenge of simultaneously optimizing surface adsorptions towards different adsorbates. Herein, we overcome this challenge by tuning atomic MoOx layer with high oxophilicity onto PtMo nanoparticles with the optimized Had, OHad and COad adsorptions for boosting anti‐CO poisoning hydrogen cycle electrocatalysis in alkaline media. For alkaline HOR, this catalyst exhibits a high kinetic and an exchange current density of 3.19 mA μgPt−1 at 50 mV versus RHE and 0.83 mA cmPt−2, 10.3 and 3.8‐fold higher than those of commercial Pt/C, respectively. For alkaline HER, it achieves an unprecedented overpotential of 37 mV at 10 mA cm−2. Experimental and theoretical studies show that the orchestrated electronic and oxophilic regulation of PtMo/MoOx interface nanoparticles simultaneously optimize Had and OHad adsorption for boosting alkaline hydrogen electrocatalysis, whereas reactive oxygen from amorphous MoOx atomic layer lowers the CO oxidation reaction barrier, leading to superior anti‐poisoning ability even at 100 ppm CO. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology