Increased CO2 Affinity and Adsorption Selectivity in MOF-801 Fluorinated Analogues
Diletta Morelli Venturi,Maria Sole Notari,Roberto Bondi,Edoardo Mosconi,Waldemar Kaiser,Giorgio Mercuri,Giuliano Giambastiani,Andrea Rossin,Marco Taddei,Ferdinando Costantino
DOI: https://doi.org/10.1021/acsami.2c07640
2022-09-14
Abstract:The novel ZrIV-based perfluorinated metal-organic framework (PF-MOF) [Zr6O4(OH)4(TFS)6] (ZrTFS) was prepared under solvent-free conditions using the commercially available tetrafluorosuccinic acid (H2TFS) as a bridging ditopic linker. Since H2TFS can be seen as the fully aliphatic and perfluorinated C4 analogue of fumaric acid, ZrTFS was found to be isoreticular to zirconium fumarate (MOF-801). The structure of ZrTFS was solved and refined from X-ray powder diffraction data. Despite this analogy, the gas adsorption capacity of ZrTFS is much lower than that of MOF-801; in the former, the presence of bulky fluorine atoms causes a considerable window size reduction. To have PF-MOFs with more accessible porosity, postsynthetic exchange (PSE) reactions on (defective) MOF-801 suspended in H2TFS aqueous solutions were carried out. Despite the different H2TFS concentrations used in the PSE process, the exchanges yielded two mixed-linker materials of similar minimal formulae [Zr6O4(μ3-OH)4(μ1-OH)2.08(H2O)2.08(FUM)4.04(HTFS)1.84] (PF-MOF1) and [Zr6O4(μ3-OH)4(μ1-OH)1.83(H2O)1.83(FUM)4.04(HTFS)2.09] (PF-MOF2) (FUM2- = fumarate), where the perfluorinated linker was found to fully replace the capping acetate in the defective sites of pristine MOF-801. CO2 and N2 adsorption isotherms collected on all samples reveal that both CO2 thermodynamic affinity (isosteric heat of adsorption at zero coverage, Qst) and CO2/N2 adsorption selectivity increase with the amount of incorporated TFS2-, reaching the maximum values of 30 kJ mol-1 and 41 (IAST), respectively, in PF-MOF2. This confirms the beneficial effect coming from the introduction of fluorinated linkers in MOFs on their CO2 adsorption ability. Finally, solid-state density functional theory calculations were carried out to cast light on the structural features and on the thermodynamics of CO2 adsorption in MOF-801 and ZrTFS. Due to the difficulties in modeling a defective MOF, an intermediate structure containing both linkers in the framework was also designed. In this structure, the preferential CO2 adsorption site is the tetrahedral pore in the "UiO-66-like" structure. The extra energy stabilization stems from a hydrogen bond interaction between CO2 and a hydroxyl group on the inorganic cluster.