Synthesis and characterization of the interpenetrated MOF-5
Bi Chen,Xiujian Wang,Qianfeng Zhang,Xiaoyong Xi,Jingjing Cai,Huang Qi,Si Shi,Jie Wang,Dan Yuan,Min Fang
DOI: https://doi.org/10.1039/b922528e
2010-01-01
Journal of Materials Chemistry
Abstract:MOF-5 is an important metal–organic framework and has been intensely studied, especially in its hydrogen storage properties. In this study, we obtained the interpenetrated MOF-5 materials (MOF-5-int) using N,N′-dimethylformamide (DMF) or N,N′-diethylformamide (DEF) as solvents. The Langmuir surface area of MOF-5-int determined by N2 adsorption is 950–1100 m2 g−1, much lower than the non-penetrated MOF-5 (3000 m2 g−1). However, it can store 1.54–1.82 wt% by volumetric method hydrogen at 77 K and 1 atm, which is higher than the amount stored by the non-penetrated MOF-5. The MOF-5-int was also characterized by XRD-powder diffraction, thermogravimetric analysis (TGA), nitrogen adsorption/desorption analysis, scanning electron microscope (SEM) and X-ray single-crystal structure diffraction. In addition, we found grinding greatly facilitates the decomposition of the MOF-5-int material by H2O to a nonporous phase ZnBDC·xH2O (within 2–5 min, BDC = 1,4-benzenedicarboxylate), even under low humidity (30%), which calls for careful handling of the MOF-5 material. The effects of the water content, reaction time, reaction temperature, molar ratio of Zn(NO3)2 to H2BDC, addition of H2O2, rapid stirring and dilution on the synthesis of MOF-5-int were studied and the synthetic conditions were optimized. Moreover, Hafizovic et al. (J. Am. Chem. Soc., 2007, 129, 3612) found the intensity ratio of the powder XRD peak at 9.7° to that at 6.8° (referred to as the R1 value) of MOF-5 can be used to predict its porosity. The lower the intensity ratio, the more porous it is. In this study, we showed that MOF-5-int can have a very low R1 value but also a low porosity. The low specific surface area (SSA) is mainly due to its interpenetrated structure instead of the entrapped zinc species or the mesopores in the material, as previously proposed in the literature, and associated with the characteristic, very strong peak at 13.8° in its XRD-powder diffraction pattern. A high R2 value (the ratio of the intensity of the peak at 13.8° to that at 6.8°) suggests an interpenetrated structure, especially when the R1 value is low. In addition, we found that although entrapped ZnO or solvent molecules can increase the R1 value, and a low R1 value implies no zinc species or solvent molecules entrapped in the MOF-5 framework, a high R1 value does not necessarily suggest the presence of entrapped molecules.