Corrosion and Stress Corrosion Resistance of Al Zn Alloy 7075 by Nano-Polymeric Coatings

Amal M. Abdel-Karim,Ashraf M. El-Shamy,Y. Reda

DOI: https://doi.org/10.1007/s40735-022-00656-2

2022-03-19

Abstract:Al–Zn alloy 7075 has been broadly considered owing to its exceptional machinery possessions established by age hardening and extensive uses. For instance, the creation of stress corrosion cracking is an example of stress corrosion. Stress corrosion cracking is caused by a corrodent reacting with long-term, continuous tensile stress. Stress corrosion cracking is sometimes referred to as stress corrosion cracking or stress corrosion cracking. It is characterized by corrosion in the microscopic granular composition of a metal's surface, which leads to the production of a rusty surface on the metal's surface. Small cracks on the metallic surface are formed as a consequence of the application of stresses (applied or residual), which causes the boundaries to open and cracks to emerge. It is noticed from the values of corrosion potential and Rp increased, while the values of corrosion current density and corrosion rate are diminished by polyurethane PU coating more than polyamide PA and nitrocellulose NC, confirming that PU coverings afford an operative shield against deterioration of Al7075, suggesting the excessive possibility for application in industry. The morphology of Al alloy coated with polymer was characterized using SEM. The PU is recommended as a coating polymer for shielding the surface of Al.