Abstract:Efficient and stable electrode materials are urgently required for wastewater treatment in the electrocatalytic degradation of toxic and refractory organic pollutants. Ti3+ self-doping black TiO2 nanotube arrays (Ti/B-TiO2-NTs) as an interlayer were used for preparing a novel PbO2 electrode via an electrochemical reduction technology, and a sodium dodecyl sulfate (SDS)-modified PbO2 catalytic layer was successfully achieved via an electrochemical deposition technology. The physicochemical characterization tests showed that the Ti/B-TiO2-NTs/PbO2-SDS electrodes have a denser surface and finer grain size with the introduction of Ti3+ in the interlayer of Ti/TiO2-NTs and the addition of SDS in the active layer of PbO2. The electrochemical characterization results showed that the Ti3+ self-doping black Ti/TiO2-NTs/PbO2-SDS electrode had higher oxygen evolution potential (2.11 V vs. SCE), higher electrode stability, smaller charge-transfer resistance (6.74 Ω cm−2), and higher hydroxyl radical production activity, leading to it possessing better electrocatalytic properties. The above results indicated that the physicochemical and electrochemical characterization of the PbO2 electrode were all enhanced significantly with the introduction of Ti3+ and SDS. Furthermore, the Ti/B-TiO2-NTs/PbO2-SDS electrodes displayed the best performance on the degradation of methylene blue (MB) in simulated wastewater via bulk electrolysis. The removal efficiency of MB and the chemical oxygen demand (COD) could reach about 99.7% and 80.6% under the optimal conditions after 120 min, respectively. The pseudo-first-order kinetic constant of the Ti/B-TiO2-NTs/PbO2-SDS electrode was 0.03956 min−1, which was approximately 3.18 times faster than that of the Ti/TiO2-NTs/PbO2 electrode (0.01254 min−1). In addition, the Ti/B-TiO2-NTs/PbO2-SDS electrodes showed excellent stability and reusability. The degradation mechanism of MB was explored via the experimental identification of intermediates. In summary, the Ti3+ self-doping black Ti/TiO2-NTs/PbO2-SDS electrode is a promising electrode in treating wastewater.

Preparation of TiO2@Sn(Sb)O2 core–shell composites and their applications for electrocatalytic degradation of methylene blue

Dye wastewater treatment using self-made Nd doped Ti/SnO2-Sb electro-catalytic electrodes

A facile electroless preparation of Cu, Sn and Sb oxides coated Ti electrode for electrocatalytic degradation of organic pollutants

Fabrication of SnO2/TiO2 composite by a chemical co-precipitation method for efficient electrocatalytic oxidation of methylene blue

Electrochemical degradation of methylene blue by Pb modified porous SnO 2 anode

Photocatalyst-coated Carbon Microtube Electrodes: Preparation and Characterization of Their Properties and Photocatalytic Degradation of Methylene Blue.

Development of SDS-Modified PbO2 Anode Material Based on Ti3+ Self-Doping Black TiO2NTs Substrate as a Conductive Interlayer for Enhanced Electrocatalytic Oxidation of Methylene Blue

Preparation of Yb-Sb co-doped Ti/SnO2 electrode for electrocatalytic degradation of sulfamethoxazole (SMX)

Ti/SnO[sub 2]–sb Electrodes for Pollutant Degradation Prepared Using Ultrasonic Spray Pyrolysis

Fabrication of Fe2O3/TiO2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Preparation of a novel Ce and Sb co-doped SnO2 nanoflowers electrode by a two-step (hydrothermal and thermal decomposition) method for organic pollutants electrochemical degradation

Efficient photocatalytic degradation of aqueous organic pollutants by using an advanced TiO2/Ti3C2/montmorillonite composites

Synthesis of a novel Ti/TiO 2 Blue/SnO 2 -Sb@Ni-La electrode and the way to improve the degradation efficiency of some organic pollutants in electrochemical process using Ti/TiO 2 Blue/SnO 2 -Sb@Ni-La as anode

The spent FCC catalyst loaded with Sb-doped SnO2 and its application in electrocatalytic degradation of methylene blue

Efficient catalytic degradation of methylene blue by a novel Fe3+-TiO2@CGS three-dimensional photoelectric system

Application of the synergistic Ti/SnO 2 –Sb–Cu anode and Ti/ZnO/CuO cathode in the electrochemical treatment of wastewater

Study on Preparation of Modified Ti-Based Lead Dioxide Electrode and Degraded Methylene Blue

Preparation of SnS2/TiO2 by a thermo-solvent ultrasonic method and its high photo-catalytic performance for decontamination under visible light

[Effect of Heat Treatment on the Electrocatalytic Activity of SnO2/Ti Anode in Degradation of P-Benzoquinone].

Antimony and Cerium Co-Doped Tin Oxide Electrodes for Pollutant Degradation

Preparation and performance of highly active and long-life mesopore Ti/SnO2–Sb electrodes for electrochemical degradation of phenol