Solvothermal preparation of Co-doped CoxV6−xO13 of cathode materials for lithium-ion batteries

Huanhuan Zhang,Zhengguang Zou,Shengyu Li,Yanjiao Zhang,Shuchao Zhang,Jie Liu

DOI: https://doi.org/10.1007/s10854-020-04997-x

2021-01-01

Abstract:V6O13 cathode materials have received great attention owing to its high theoretical specific capacity and energy density; however, the poor cycle stability and rate performance have constrained their development. In this experiment, the nanorod-like Co-doped V6O13 with a theoretical equation of CoxV6−xO13 was synthesized for the first time by one-step solvothermal method, and investigated with X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and tests of electrochemical performances. When x = 0.03, the material shows the best electrochemical performance, the sample has the best discharge specific capacity of 377.3 mAh/g at the beginning, and the capacity retention is 54.4% after 100 cycles at 0.1 C (42 mA/g), comparing with those of the pure V6O13 only 279.4 mAh/g and 37.6% in the same condition. The increase in specific surface area and structural stability promoted the kinetics of the chemical reaction and improved the electrochemical properties of the material. The applicability of this method was further examined through a series of tests and analysis of disassembled batteries after cycle, and the evidences that proper Co doping can stable the structure of materials are provided.