Optimizing the lithium storage property of sodium lithium titanate via oxygen-site doping

Siyun Ren,Fang Wang,Pei Wang,Pengfei Wang,Xiaoying Song,Yi Huang,U-Fat Chio,Wei Wang

DOI: https://doi.org/10.1007/s11581-020-03895-w

IF: 2.961

2021-01-13

Ionics

Abstract:<p class="a-plus-plus">Two modified products of Na<sub class="a-plus-plus">2</sub>Li<sub class="a-plus-plus">2</sub>Ti<sub class="a-plus-plus">6</sub>O<sub class="a-plus-plus">14</sub> were prepared via O-site replacement by F<sup class="a-plus-plus">−</sup> and Cl<sup class="a-plus-plus">−</sup> doping and employed to store lithium during cycles. Through tests of structure and electrochemical properties, it seems that substituting part of the O-site for low-valent ions enables better ionic and electronic conductivities of pristine Na<sub class="a-plus-plus">2</sub>Li<sub class="a-plus-plus">2</sub>Ti<sub class="a-plus-plus">6</sub>O<sub class="a-plus-plus">14</sub>. As a consequence, the modified products exhibit preferable electrochemical performance when compared with the pristine one, especially for the Na<sub class="a-plus-plus">2</sub>Li<sub class="a-plus-plus">2</sub>Ti<sub class="a-plus-plus">6</sub>O<sub class="a-plus-plus">13.7</sub>F<sub class="a-plus-plus">0.3</sub>, which displays the best reversible charge specific capacity of 121.20 mAh g<sup class="a-plus-plus">−1</sup> and the battery was tested at 100 mA g<sup class="a-plus-plus">−1</sup>. Moreover, in situ XRD results explain that the great reversibility of structure is significant to the excellent lithium storage property of Na<sub class="a-plus-plus">2</sub>Li<sub class="a-plus-plus">2</sub>Ti<sub class="a-plus-plus">6</sub>O<sub class="a-plus-plus">13.7</sub>F<sub class="a-plus-plus">0.3</sub> for the rechargeable lithium-ion batteries.</p>

chemistry, physical,physics, condensed matter,electrochemistry