Improved transparency and conferred luminescence property via Er3+/Ho3+ co-doped in KNN-based ceramics
Nuo Wang,Shaoyang Shi,Jianpeng Ye,Zhongwang Bi,Wei Qiu,Jiwen Xu,Ling Yang,Hua Wang
DOI: https://doi.org/10.1007/s10854-024-13683-1
2024-10-18
Journal of Materials Science Materials in Electronics
Abstract:Transparent luminescent ceramics have broad application prospects in fields such as optical switches, optical communication, and optical storage. 0.94K 0.5 Na 0.5 NbO 3 –0.06Ca(Bi 0.5 Nb 0.5 )O 3 :0.4wt%Er 3+ / x wt%Ho 3+ (abbreviated as KNN-0.06CBN:Er 3+ / x Ho 3+ , x = 0.1, 0.2, 0.3, 0.4, 0.5) transparent fluorescent ceramics were prepared by a solid-phase sintering method, in which the Er/Ho co-doped with a second component Ca(Bi 0.5 Nb 0.5 )O 3 are introduced to regulate the phase structure, grain size, and bandgap width of KNN-based ceramics for enhancing both the transparency and luminescence performance. It was found that the change in Ho content has a significant impact on the ceramic phase structure, grain size, and bandgap width while maintaining appropriate content levels of Ca(Bi 0.5 Nb 0.5 )O 3 and Er. The KNN-0.06CBN: Er 3+ / x wt%Ho 3+ ceramics with different Ho content both exhibit pseudo cubic phase, but an increase in the content of the rare earth element Ho 3+ will lead to the ceramic grain size decreases firstly and then increases, at the same time the value of optical bandgap increases first and then decreases. When the Ho content x is 0.1, KNN-0.06CBN: Er 3+ / x Ho 3+ ceramics achieve excellent up-conversion luminescence performance with two weak green light emissions at 531, 549 nm, respectively, and a strong red emission at 660 nm, while ensuring high transmittance of 59% at 780 nm in the visible region and 69% at 1100 nm in the near infrared region, benefiting by the smaller grain size and higher E g value.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied